Rapidly solidified powder metallurgy Mg97Zn1Y2Alloys with excellent tensile yield strength above 600 MPa

Nanocrystalline magnesium alloys having high tensile strength, high elevated-temperature tensile strength, high-strain-rate superplasticity and high thermal stability have been developed in Mg97Zn1Y2 (at%) alloy by rapidly solidified powder metallurgy (RS P/M) processing. The tensile yield strength and elongation that were dependent on the consolidation temperature were in the ranges of 480 to 610MPa and 5 to 16%., respectively. Young's modulus of the RS P/M alloy was 45 GPa. The specific tensile yield strength was four times as high as, that of a commercial AZ91-T6 alloy, and was higher than those of conventional titanium (Ti-6Al-4V) and aluminum (7075-T6) alloys. The RS P/M alloys exhibited excellent elevated-temperature yield strength that was 510 MPa at 423 K. The RS P/M alloy also exhibited high-strain-rate superplasticity at a wide strain-rate range from 1 x 10(-2) to 1 x 10(0) s(-1) and at a low temperature of 623 K. It is expected that the Mg97Zn1Y2 RS P/M alloy can be applied in some fields that requires simultaneously the high specific strength at ambient and elevated temperatures and high workability.