Photovoltaic silicon produced by thermal plasma: Influence of atomic hydrogen on oxygen elimination and passivation of the crystal defects

The photovoltaic properties of the polycrystalline silicon depend on the crystallinity and the purity of the material. The thermal plasma process gives us an alternative method of silicon preparation since it is possible to produce an ultrahigh purity with simultaneously a passivation of crystalline defects and active impurities. We demonstrate the efficiency of the plasma purification process and particularly the influence of the atomic hydrogen in an argon thermal plasma on the photovoltaic properties of silicon. The results of the diffusion lengths measured by the photoelectrochemical method show that locally it rises up to 200 mu m. We correlate these photovoltaic measurements with the properties of the crystal (defects and purity) by means of measurements by Fourier transform infrared spectroscopy (FTIR) at low temperature (6 K), four probes resistivity technique, scanning electronic microscopy, inductively coupled plasma (ICP), and neutronic activation analyses. We show that the increase of the purity explains the high measured diffusion lengths. Nevertheless, the thermal conditions of the crystallization of the silicon, due to the specificity of the plasma, lead to defects such as dislocations for which density is particularly high (>10(6) dis/cm(2)). The results show that chemical reactions between the atomic hydrogen of the plasma and the oxygen of the silicon occur. They decrease the oxygen content in silicon from 3 x 10(17) at./cm(3) down to 2 x 10(16) at./cm(3), while the residual hydrogen in silicon is close to 2 x 10(15) at./cm(3). This passivates the dangling bonds of ultrapure silicon with a high thermal stability up to 1000 K, The objective of this paper is to demonstrate that the hydrogen in the plasma modifies the electronic properties of the material to achieve a very good photocurrent even though the dislocation density of the silicon is very high.