On the preparation and composition of potassium promoted iron oxide model catalyst films

被引:71
作者
Joseph, Y [1 ]
Ketteler, G [1 ]
Kuhrs, C [1 ]
Ranke, W [1 ]
Weiss, W [1 ]
Schlögl, R [1 ]
机构
[1] Max Planck Gesell, Fritz Haber Inst, Dept Inorgan Chem, D-14195 Berlin, Germany
关键词
D O I
10.1039/b104263g
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Potassium promoted iron oxide model catalyst films were prepared by deposition of potassium onto epitaxial Fe3O4 (111) Elms at 200 K, followed by annealing in the range 200 to 970 K. Their formation and composition were investigated by X-ray photoelectron spectroscopy (XPS) in combination with thermal desorption spectroscopy (TDS) and thermodynamic considerations. Already at 300 K a solid-state reaction occurred and the iron oxide was partly reduced. Around 700 K a KFeO2 phase identified which transformed at higher temperatures into KxFe22O34(0.67 < x < 4). This transformation started the bulk of the film so that initially a potassium-rich KFeO2 layer was formed on top of KxFe22O34. The formation of a single-crystalline KxFe22O34 (x = 0.67) layer, which is terminated by a submonolayer of potassium, is assumed to occur at 970 K. For a certain potassium content, this surface develops a well ordered phase with a (2 x 2) superstructure. The potassium containing phases are not stable in water atmosphere: In 10(-8) mbar H2O, potassium hydroxide forms, then decomposes and desorbs beyond 400-500 K resulting in a potassium-depleted near-surface layer.
引用
收藏
页码:4141 / 4153
页数:13
相关论文
共 50 条
[1]  
BARIN I, 1992, THERMOCHEMICAL DATA
[2]   ADSORPTION OF H2O ON POTASSIUM FILMS [J].
BONZEL, HP ;
PIRUG, G ;
WINKLER, A .
SURFACE SCIENCE, 1986, 175 (02) :287-312
[3]  
BONZEL HP, 1989, PHYSICS CHEM ALKALI
[4]   CORE AND VALENCE LEVEL PHOTOEMISSION STUDIES OF IRON-OXIDE SURFACES AND OXIDATION OF IRON [J].
BRUNDLE, CR ;
CHUANG, TJ ;
WANDELT, K .
SURFACE SCIENCE, 1977, 68 (01) :459-468
[5]   Adsorption and oxidation of K deposited on graphite [J].
Caballero, A ;
Espinos, JP ;
Fernandez, A ;
Soriano, L ;
GonzalezElipe, AR .
SURFACE SCIENCE, 1996, 364 (03) :253-265
[6]   The formation and characterisation of Ni3+ -: an X-ray photoelectron spectroscopic investigation of potassium-doped Ni(110)-O [J].
Carley, AF ;
Jackson, SD ;
O'Shea, JN ;
Roberts, MW .
SURFACE SCIENCE, 1999, 440 (03) :L868-L874
[7]  
DVORETSKII NV, 1989, INORG MATER+, V25, P242
[8]  
DVORETSKII NV, 1991, INORG MATER+, V27, P1064
[9]  
ELIEZER I, 1978, HIGH TEMP SCI, V10, P1
[10]   CRITICAL-EVALUATION AND OPTIMIZATION OF THE THERMODYNAMIC PROPERTIES AND PHASE-DIAGRAMS OF THE MGO-AL2O3, MNO-AL2O3, FEO-AL2O3, NA2O-AL2O3 AND K2O-AL2O3 SYSTEMS [J].
ERIKSSON, G ;
WU, P ;
PELTON, AD .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 1993, 17 (02) :189-205