The influence of hBN crystallinity and additive Lithium hydride on cBN synthesis in Li3N-hBN system

被引:8
作者
Du, Yonghui [1 ]
Ji, Xiaorui [1 ]
Yang, Xuxin [1 ]
Gong, Xiliang [1 ]
Yang, Dapeng [1 ]
Su, Zuopeng [1 ]
Zhang, Tiechen [1 ]
机构
[1] Jilin Univ, Natl Lab Superhard Mat, Changchun 130012, Peoples R China
关键词
crystallinity; lithium hydride; high pressure and temperature;
D O I
10.1016/j.diamond.2006.12.014
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In this paper, the influence of hBN crystallinity and additive Lithium hydride (LiH) on cBN synthesis with Lithium nitride (Li3N) as catalyst was investigated under the pressure of 4.5-5 GPa and the temperature of 1500-1700 degrees C. hBN with different crystallinities was obtained by the same hBN. Some were explored to high pressure and high temperature, and others were subjected to heat treatment with alkali. X-ray diffraction (XRD), Raman spectroscopy and X-ray photoelectronic spectroscopy (XPS) were used to characterize the property of the starting materials. The synthesized samples were observed by optical microscopy (OM). The results indicated that besides the crystallinity of hBN, which is a general parameter for controlling the structural quality of hBN powders, some other factors such as the content of B+ at the surface of hBN and additive LiH all strongly influence the synthesis of cBN. (c) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码:1475 / 1478
页数:4
相关论文
共 21 条
[11]  
KUDAKA K, 1966, J CHEM SOC JAPAN, V69, P365
[12]   In situ observation of the crystallization of amorphous boron nitride at high pressures and temperatures [J].
Lorenz, H ;
Orgzall, I .
SCRIPTA MATERIALIA, 2005, 52 (06) :537-540
[13]   The influence of the h-BN morphology and structure on the c-BN growth [J].
Nistor, L ;
Teodorescu, V ;
Ghica, C ;
Van Landuyt, J ;
Dinca, G ;
Georgeoni, P .
DIAMOND AND RELATED MATERIALS, 2001, 10 (3-7) :1352-1356
[14]  
Saito H., 1970, YOGYO-KYOKAI-SHI, V74, P7
[15]   ON THE LOW-PRESSURE SYNTHESIS OF CUBIC BORON-NITRIDE [J].
SINGH, BP ;
SOLOZHENKO, VL ;
WILL, G .
DIAMOND AND RELATED MATERIALS, 1995, 4 (10) :1193-1195
[16]  
Su ZP, 2006, CHINESE PHYS LETT, V23, P2285, DOI 10.1088/0256-307X/23/8/088
[17]  
THOMAS J, 1963, J AM CHEM SOC, V84, P4619
[18]  
USHIO M, 1971, J CHEM SOC JAPAN IND, V74, P598
[19]   SYNTHESIS OF POLYCRYSTALLINE CUBIC BN [J].
WAKATSUK.M ;
AOKI, T ;
ICHINOSE, K .
MATERIALS RESEARCH BULLETIN, 1972, 7 (09) :999-&
[20]  
XU XW, 2001, U SCI TECHNOL, V23, P337