Mechanical characterization of the flax/epoxy composite material

被引:22
作者
Cerbu, Camelia [1 ]
机构
[1] Transilvania Univ Brasov, Brasov 500036, Romania
来源
8TH INTERNATIONAL CONFERENCE INTERDISCIPLINARITY IN ENGINEERING, INTER-ENG 2014 | 2015年 / 19卷
关键词
composite material; flax; tensile test; bending; Charpy;
D O I
10.1016/j.protcy.2015.02.039
中图分类号
TP39 [计算机的应用];
学科分类号
081203 ; 0835 ;
摘要
The paper focuses on the mechanical characterization of the composite material made of epoxy resin reinforced with flax fabric. The mechanical behavior of flax / epoxy composite material was analyzed by using tensile test, flexural (bending) test and impact test (Charpy method). After the statistical processing of the experimental data recorded for all specimens tested, the average values of the following properties are determinate: Young's modulus E in tension, tensile normal stress at failure, tensile normal strain at failure,Yotmg's modulus in bending, flexural normal stress at failure, strain energy in all tests (tension, bending, Charpy), resilience recorded in Charpy test. Finally, it reports the average values of the mechanical properties of the flax / epoxy composite material tested. The results show that the average values of the mechanical characteristics recorded on the weft direction of the flax fabric are greater than the ones recorded on the warp direction. (C) 2015 Published by Elsevier Ltd.
引用
收藏
页码:268 / 275
页数:8
相关论文
共 9 条
[1]   Estimation of the tensile strength of an oriented flax fiber-reinforced polymer composite [J].
Andersons, J. ;
Joffe, R. .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2011, 42 (09) :1229-1235
[2]  
[Anonymous], 2001, 17912001 SR EN ISO
[3]  
[Anonymous], 141252000 SR EN ISO
[4]  
[Anonymous], 52742000 SR EN ISO
[5]  
Camelia Cerbu, 2010, MAT PLASTICE, V47, P109
[6]  
Camelia Cerbu, 2009, ANN U PETROSANI MECH, V11, P29
[7]  
Curtu I, 2012, MATER PLAST, V49, P68
[8]   The fracture behaviour and toughness of woven flax fibre reinforced epoxy composites [J].
Liu, Q. ;
Hughes, M. .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2008, 39 (10) :1644-1652
[9]   Analysis of effect of fiber orientation on Young's modulus for unidirectional fiber reinforced composites [J].
Wang, H. W. ;
Zhou, H. W. ;
Gui, L. L. ;
Ji, H. W. ;
Zhang, X. C. .
COMPOSITES PART B-ENGINEERING, 2014, 56 :733-739