Mechanical and swelling behavior of double networked natural rubber cured using a new binary accelerator system

The concept of double networks, which impart chain orientation to elastomers, is a rather new idea. Double networks were induced in natural rubber vulcanizates cured with different accelerator systems. Double networked natural rubber with different extensions cured with N-cyclohexyl benzothiazyl sulphenamide (CBS) and 1-phenyl 5-ortho -tolyl 2,4 dithiobiuret was studied and the effect of extension on the mechanical properties and swelling was analyzed. The extent of chain orientation was analyzed through anisotropic swelling studies. The modulus, tensile strength and tear strength showed an increase with increased residual extension ratio. The effect was more predominant in the longitudinal direction than in the transverse direction. The ultimate tensile elongation showed a slight deterioration. It was revealed that the formation of double networks with higher residual extension ratios restricted the entry of the solvent. Based on the studies it was concluded that residual extension has a profound effect in determining the final properties of vulcanizates.