As-deposited mixed zone in thermally grown oxide beneath a thermal barrier coating

被引:64
作者
Murphy, KS
More, KL
Lance, MJ
机构
[1] Howmet Res Corp Howmet Castings, Alcoa Business, Whitehall, MI 49461 USA
[2] Oak Ridge Natl Lab, Oak Ridge, TN 37831 USA
关键词
phase transitions; transmission electron microscopy; electron beam evaporation; pack diffusion coatings; zirconium oxide; thermally grown oxide;
D O I
10.1016/S0257-8972(01)01371-8
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Gas turbine designers are increasingly using electron-beam physical vapor deposited (EB-PVD) thermal barrier coatings (TBC) to meet the challenge of higher efficiency gas turbine engine requirements. A key feature for expanding the use of TBCs is increased spallation life and reduced spallation life variability. Such a coating system comprises a substrate (Ni-based single crystal alloy), a bond coat (diffusion aluminide or MCrAlY), a ceramic (7 wt.% yttria stabilized zirconia), and a thin thermally grown oxide (TGO) between the bond coat and the ceramic. The TGO is intended to be alpha -alumina. but evidence reported by other researchers suggests that in some cases the alpha -deposited TGO may not be entirely ot-alumina. The thin nature of the TGO in as-deposited TBCs (< 0.5 mum) makes analysis of the phases present and morphology difficult. Advancements in transmission electron microscopy (TEM) sample preparation and photo-stimulated luminescence spectroscopy (PSLS) have allowed higher quality and easier characterization of the TGO. In this study, EB-PVD TBCs were applied to platinum-aluminide bond coats on a Ni-based superalloy. Three types of coatings were produced by changing one PVD process variable. The as-processed TGO layer was characterized utilizing scanning transmission electron microscopy (STEM) and PSLS for each of the three coating process variables used. Results of this work found that the TGO comprised two sublayers; (1) a continuous layer of gamma -Al2O3 between the mixed oxide zone and the bond coat; and (2) a mixed oxide zone between the continuous gamma -Al2O3 and the TBC layer. An explanation for the creation of the mixed oxide zone found in these TGO morphologies is presented. (C) 2001 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:152 / 161
页数:10
相关论文
共 19 条
[1]  
Bose S., 1995, P THERMAL BARRIER CO, P63
[2]   Nondestructive evaluation of the oxidation stresses through thermal barrier coatings using Cr3+ piezospectroscopy [J].
Christensen, RJ ;
Lipkin, DM ;
Clarke, DR ;
Murphy, K .
APPLIED PHYSICS LETTERS, 1996, 69 (24) :3754-3756
[3]  
DRAVID V, 1998, HITACHI INSTRUM NEWS, V34, P3
[4]  
ERICKSON GL, 1997, ADV MATER PROCESS, P29
[5]   Stress development in alumina scales formed upon oxidation of (111)NiAl single crystals [J].
Lipkin, DM ;
Clarke, DR ;
Hollatz, M ;
Bobeth, M ;
Pompe, W .
CORROSION SCIENCE, 1997, 39 (02) :231-242
[6]   Lateral growth kinetics of alpha-alumina accompanying the formation of a protective scale on (111)NiAl during oxidation at 1100 degrees C [J].
Lipkin, DM ;
Schaffer, H ;
Adar, F ;
Clarke, DR .
APPLIED PHYSICS LETTERS, 1997, 70 (19) :2550-2552
[7]  
MILLER RA, 1995, NASA CP, V3312, P17
[8]  
MORE KL, 2000, P MICROSC MICROANAL, V6, P540
[9]   Erosion of EB-PVD thermal barrier coatings [J].
Nicholls, JR ;
Jaslier, Y ;
Rickerby, DS .
MATERIALS AT HIGH TEMPERATURES, 1998, 15 (01) :15-22
[10]   A comparison between the erosion behaviour of thermal spray and electron beam physical vapour deposition thermal barrier coatings [J].
Nicholls, JR ;
Deakin, MJ ;
Rickerby, DS .
WEAR, 1999, 233 :352-361