Nanostructural aspects of wear in ion-beam deposited Pb-Mo-S films

被引：8

作者：

Dunn, DN ^{[1
]}

Wahl, KJ ^{[1
]}

Singer, IL ^{[1
]}

机构：

[1] USN, Res Lab, Tribol Sect, Washington, DC 20375 USA

来源：

FUNDAMENTALS OF NANOINDENTATION AND NANOTRIBOLOGY | 1998年 / 522卷

关键词：

D O I：

10.1557/PROC-522-451

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Microstructural aspects of wear resistance have been investigated using cross-sectional transmission electron microscopy (TEM) to analyze both as-deposited and worn films. As-deposited Pb-Mo-S films were virtually amorphous, i.e., show no long range structure. Wear tracks revealed a two-part wear process localized at the sliding surface. First, Pb-Mo-S at the sliding surface was transformed into basal-oriented, crystalline MoS2 from 1 to 4 monolayers thick. Then, as sliding continued, the MoS2 layers were detached one or two layers at a time. Evidence for the nanometer scale wear process is presented.