Structure and properties of chromium- and zinc-oxide layers formed on Zircaloy-2 in high-temperature water

被引:1
作者
Blajiev, OL [1 ]
Matsuura, C [1 ]
Hiroishi, D [1 ]
Ishigure, K [1 ]
机构
[1] Univ Tokyo, Dept Nucl Engn, Tokyo 113, Japan
关键词
Zircaloy; corrosion; zinc-chemistry;
D O I
10.13182/NT02-A3257
中图分类号
TL [原子能技术]; O571 [原子核物理学];
学科分类号
0827 ; 082701 ;
摘要
The corrosion behavior of Zircaloy-2 in the presence of Zn was investigated. Zinc is a possible technological additive to be injected in the coolant to reduce the Co-60 buildup. However, its influence on the cladding corrosion, alone or in combination with some typical corrosion impurities, as, for example, Cr, has not been considered so far. Because of this, the surface composition and electrochemical properties of Zircaloy specimens were investigated after their exposure to Zn2+, CrO42-, and CrO42- + Zn2+ aqueous solutions at 250 degreesC. It was found that zinc-containing phases did not deposit from solutions containing on Zn2+ ions. Amorphous Cr3+= oxide and ZnCr2O4 ferrite phases were found on the surface of the samples after their exposure to CrO42- and CrO42- + Zn2+ environments, respectively. The amounts of the deposited Cr and Zn + Cr strongly depended on the times of the preconditioning of the Zircaloy specimens in high-temperature water. The rate of the oxide precipitation declined with increasing exposure time to both the CrO42- and CrO42- + Zn2+ solutions. The electrochemical measurement showed that the limiting factor of the Cr and Zn + Cr deposition reaction was the reduction of Cr(VI) to Cr(III). The reduction completely depended on the resistance of ZrO2, Cr, and Zn + Cr oxides, which increased with the time of preconditioning and exposure. A thermodynamic analysis based on oxide solubilities was applied to explain the different deposition pathways in the CrO42- andCrO(4)(2-) + Zn2+ environments. In view of the decreasing deposition rate of the Zn - Cr-oxide phases, it could be concluded that their limited precipitation and presence do not have a significant adverse effect on the fuel cladding corrosion.
引用
收藏
页码:60 / 71
页数:12
相关论文
共 10 条
[1]  
BLAJIEV O, 1999, ANN M AT EN SOC JAP
[2]  
COWAN RL, 2000, WATER CHEM NUCL REAC, V8, P97
[3]   Redistribution of the alloying elements during Zircaloy-2 oxidation [J].
Cox, B ;
Sheikh, HI .
JOURNAL OF NUCLEAR MATERIALS, 1997, 249 (01) :17-32
[4]   Hydrolysis of zinc ion and solubility of zinc oxide in high-temperature aqueous systems [J].
Hanzawa, Y ;
Hiroishi, D ;
Matsuura, C ;
Ishigure, K ;
Nagao, M ;
Haginuma, M .
NUCLEAR SCIENCE AND ENGINEERING, 1997, 127 (03) :292-299
[5]  
KELEN T, 2000, WATER CHEM NUCL REAC, V8, P103
[6]  
Matsuura C, 1998, P INT C WAT CHEM NUC, P847
[7]  
MOCHIZUKI K, 2000, WATER CHEM NUCL REAC, V8, P142
[8]   QUANTITATIVE CHEMICAL-ANALYSIS BY ESCA [J].
PENN, DR .
JOURNAL OF ELECTRON SPECTROSCOPY AND RELATED PHENOMENA, 1976, 9 (01) :29-40
[9]   HARTREE-SLATER SUBSHELL PHOTOIONIZATION CROSS-SECTIONS AT 1254 AND 1487EV [J].
SCOFIELD, JH .
JOURNAL OF ELECTRON SPECTROSCOPY AND RELATED PHENOMENA, 1976, 8 (02) :129-137
[10]  
Spenke E., 1958, ELECT SEMICONDUCTORS