Effect of Ni on vacancy concentrations and hardness in FeAl alloys

被引:17
作者
Pike, LM
Liu, CT
Chang, YA
机构
[1] Oak Ridge Natl Lab, Div Met & Ceram, Oak Ridge, TN 37831 USA
[2] Univ Wisconsin, Dept Mat Sci & Engn, Madison, WI 53706 USA
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1998年 / 29卷 / 07期
基金
美国能源部;
关键词
D O I
10.1007/s11661-998-0015-3
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The effects of nickel additions to iron aluminides are investigated with respect to vacancy concentrations and solid-solution hardening. Lattice parameters, densities, vacancy concentrations, and hardnesses were measured for FeAl alloys (40, 45, 48, 50, and 51 at. pct Al) with up to 12 at. pct Ni additions, as quenched at both 700 degrees C and 1000 degrees C. It is found that Ni does not prevent the elimination of thermal vacancies, as has been suggested in previous studies. However, the equilibrium vacancy concentrations are affected by the Ni additions. No clear evidence of solid-solution hardening by the Ni additions themselves was found. Instead, it appears that the role of Ni in hardening FeAl is through the effect the Ni has on the vacancy concentration. It was found that the hardness of most of the Ni-containing FeAl alloys could be directly correlated to the square root of the vacancy concentration.
引用
收藏
页码:1911 / 1915
页数:5
相关论文
共 23 条
[1]   ALCHEMI study of site distributions of 3d-transition metals in B2-ordered iron aluminides [J].
Anderson, IM .
ACTA MATERIALIA, 1997, 45 (09) :3897-3909
[2]   CORRELATION OF THE HARDNESS AND VACANCY CONCENTRATION IN FEAL [J].
CHANG, YA ;
PIKE, LM ;
LIU, CT ;
BILBREY, AR ;
STONE, DS .
INTERMETALLICS, 1993, 1 (02) :107-115
[3]   THERMODYNAMICS AND DEFECT STRUCTURE OF INTERMETALLIC PHASES WITH THE B2 (CSCL) STRUCTURE [J].
CHANG, YA ;
NEUMANN, JP .
PROGRESS IN SOLID STATE CHEMISTRY, 1982, 14 (04) :221-301
[4]  
FLEISCHER RL, 1964, STRENGTHENING METALS, P93
[5]   INFLUENCE OF TESTING ENVIRONMENT ON THE ROOM-TEMPERATURE DUCTILITY OF FEAL ALLOYS [J].
GAYDOSH, DJ ;
NATHAL, MV .
SCRIPTA METALLURGICA ET MATERIALIA, 1990, 24 (07) :1281-1284
[6]  
HIRTH JP, 1982, THEORY DISLOCATIONS, P682
[7]   SITE PREFERENCE OF SUBSTITUTIONAL ADDITIONS TO TRIPLE-DEFECT B2 INTERMETALLIC COMPOUNDS [J].
KAO, CR ;
PIKE, LM ;
CHEN, SL ;
CHANG, YA .
INTERMETALLICS, 1994, 2 (04) :235-247
[8]   Quenched-in vacancies in B2-structured intermetallic compound FeAl [J].
Kogachi, M ;
Haraguchi, T .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 230 (1-2) :124-131
[9]  
Laves F, 1956, THEORY ALLOY PHASES
[10]   ELASTIC STIFFNESS COEFFICIENTS OF IRON-ALUMINUM ALLOYS .I. EXPERIMENTAL RESULTS AND THERMODYNAMIC ANALYSIS [J].
LEAMY, HJ ;
GIBSON, ED ;
KAYSER, FX .
ACTA METALLURGICA, 1967, 15 (12) :1827-&