The transport properties of nanocrystalline SrCe0.95Yb0.05O3 thin films

被引:35
作者
Kosacki, I
Anderson, HU
机构
[1] Department of Ceramic Engineering, University of Missouri-Rolla, Rolla
关键词
D O I
10.1063/1.116975
中图分类号
O59 [应用物理学];
学科分类号
摘要
The results of electrical transport measurements on nanocrystalline SrCe0.95Yb0.05O3 thin films are presented. Dense SrCe0.95Yb0.05O3 thin films with 30-70 nm grain size have been obtained using a spin-coating technique. These films exhibit about 10(3) higher electrical conductivity when compared with the bulk polycrystalline material. The grain size of thin films is stable to temperatures as high as 1000 degrees C since no grain-coarsening was observed. These unique electrical properties of nanocrystalline SrCe0.95Yb0.05O3 thin films are attributed to a dominant role of grain boundaries and/or interfaces. (C) 1996 American Institute of Physics.
引用
收藏
页码:4171 / 4173
页数:3
相关论文
共 12 条
[1]  
[Anonymous], [No title captured]
[2]   Solute segregation and grain-boundary impedance in high-purity stabilized zirconia [J].
Aoki, M ;
Chiang, YM ;
Kosacki, I ;
Lee, IJR ;
Tuller, H ;
Liu, YP .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1996, 79 (05) :1169-1180
[3]   OXIDE ION CONDUCTION IN YTTERBIUM-DOPED STRONTIUM CERATE [J].
BONANOS, N ;
ELLIS, B ;
MAHMOOD, MN .
SOLID STATE IONICS, 1988, 28 :579-584
[4]   SYNTHESIS AND CHARACTERIZATION OF YSZ THIN-FILM ELECTROLYTES [J].
CHEN, CC ;
NASRALLAH, MM ;
ANDERSON, HU .
SOLID STATE IONICS, 1994, 70 (pt 1) :101-108
[5]  
CHEN CC, 1995, J ELECTROCHEM SOC, V142, P2491
[6]  
CHIANG JM, 1996, APPL PHYS LETT, V69, P185
[7]   MIXED CONDUCTIVITY IN SRCE0.95YB0.05O3 PROTONIC CONDUCTORS [J].
KOSACKI, I ;
TULLER, HL .
SOLID STATE IONICS, 1995, 80 (3-4) :223-229
[8]   ELECTRICAL-PROPERTIES OF SRCE0.95YB0.05O3 IN HYDROGEN CONTAINING ATMOSPHERES [J].
KOSACKI, I ;
BECHT, JGM ;
VANLANDSCHOOT, R ;
SCHOONMAN, J .
SOLID STATE IONICS, 1993, 59 (3-4) :287-296
[9]  
KOSACKI I, 1995, SENSOR ACTUAT B-CHEM, V24, P370
[10]   ELECTRICAL-CONDUCTIVITY MEASUREMENTS ON CUPROUS BROMIDE, CUBR, IN THE PRESENCE OF OXYGEN [J].
RIESS, I ;
SAFADI, R ;
TULLER, HL .
SOLID STATE IONICS, 1993, 59 (3-4) :279-286