Long-range-ordered anodic porous alumina with less-than-30 nm hole interval

被引：30

作者：

Masuda, Hideki

Takenaka, Kensuke

Ishii, Tomohiro

Nishio, Kazuyuki

机构：

[1] Tokyo Metropolitan Univ, Dept Appl Chem, Hachioji, Tokyo 1920397, Japan

[2] KAST, Sagamihara, Kanagawa 2291131, Japan

来源：

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS | 2006年 / 45卷 / 42-45期

关键词：

anodic porous alumina; anodization; long-range ordering; sulfuric acid;

D O I：

10.1143/JJAP.45.L1165

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Long-range-ordered anodic porous alumina having hole intervals from 25 to 30 nm was prepared in H2SO4 electrolyte. Constant-voltage anodization under high temperature condition in addition to high concentration of H2SO4 generated the long-range-ordered anodic porous alumina having ideally ordered hole configuration with 25 and 30 nm hole intervals at 10 and 12 V, respectively.

引用

收藏

页码：L1165 / L1167

页数：3

相关论文

共 9 条

[1]

NANOWIRE ARRAY COMPOSITES [J].

HUBER, CA ;

HUBER, TE ;

SADOQI, M ;

LUBIN, JA ;

MANALIS, S ;

PRATER, CB .

SCIENCE, 1994, 263 (5148) :800-802

[2]

Self-ordering of cell arrangement of anodic porous alumina formed in sulfuric acid solution [J].

Masuda, H ;

Hasegwa, F ;

Ono, S .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1997, 144 (05) :L127-L130

[3]

Fabrication of gold nanodot array using anodic porous alumina as an evaporation mask [J].

Masuda, H ;

Satoh, M .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1996, 35 (1B) :L126-L129

[4]

Self-ordering of cell configuration of anodic porous alumina with large-size pores in phosphoric acid solution [J].

Masuda, H ;

Yada, K ;

Osaka, A .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1998, 37 (11A) :L1340-L1342

[5]

ORDERED METAL NANOHOLE ARRAYS MADE BY A 2-STEP REPLICATION OF HONEYCOMB STRUCTURES OF ANODIC ALUMINA [J].

MASUDA, H ;

FUKUDA, K .

SCIENCE, 1995, 268 (5216) :1466-1468

[6]

MASUDA H, 2003, 79 ANN M

[7]

Long-range-ordered anodic porous alumina with reduced hole interval formed in highly concentrated sulfuric acid solution [J].

Masuda, Hideki ;

Nagae, Mitsutaka ;

Morikawa, Takuya ;

Nishio, Kazuyuki .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 2006, 45 (12-16) :L406-L408

[8]

Aspect ratio dependence of hysteresis property of high density Co wire array buried in porous alumina template [J].

Shingubara, S ;

Morimoto, K ;

Nagayanagi, M ;

Shimizu, T ;

Yaegashi, O ;

Wu, GR ;

Sakaue, H ;

Takahagi, T ;

Takase, K .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2004, 272 :1598-1599

[9]

Patterned magnetic recording media using anodic porous alumina with single domain hole configurations of 63 nm hole interval [J].

Yasui, K ;

Morikawa, T ;

Nishio, K ;

Masuda, H .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 2005, 44 (12-15) :L469-L471