Transformation of carbon nanotubes to nanoparticles by ball milling process

被引：175

作者：

Li, YB ^{[1
]}

Wei, BQ ^{[1
]}

Liang, J ^{[1
]}

Yu, Q ^{[1
]}

Wu, DH ^{[1
]}

机构：

[1] Tsing Hua Univ, Beijing 100084, Peoples R China

来源：

CARBON | 1999年 / 37卷 / 03期

关键词：

carbon nanotubes; fullerene; phase transitions;

D O I：

10.1016/S0008-6223(98)00218-8

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Carbon nanotubes were treated by high-energy ball milling processing for different milling times, and the samples were observed by HRTEM. The broken nanotubes and lots of carbon onion-like particles were obtained in the sample milled for 15 min. When the milling time was up to 60 min, carbon nanotubes turned into amorphous carbon. On the basis of HRTEM observation of carbon nanotubes and carbon nanoparticles, we discuss the possible formation mechanism of nanoparticles under the impact acting as driving force. (C) 1999 Elsevier Science Ltd. All rights reserved.

引用

收藏

页码：493 / 497

页数：5

相关论文

共 15 条

[1] The formation, annealing and self-compression of carbon onions under electron irradiation [J].

Banhart, F ;

Fuller, T ;

Redlich, P ;

Ajayan, PM .

CHEMICAL PHYSICS LETTERS, 1997, 269 (3-4) :349-355

[2] CARBON ONIONS PRODUCED BY HEAT-TREATMENT OF CARBON SOOT AND THEIR RELATION TO THE 217.5 NM INTERSTELLAR ABSORPTION FEATURE [J].

DEHEER, WA ;

UGARTE, D .

CHEMICAL PHYSICS LETTERS, 1993, 207 (4-6) :480-486

[3] BUCKYTUBES AND DERIVATIVES - THEIR GROWTH AND IMPLICATIONS FOR BUCKYBALL FORMATION [J].

DRAVID, VP ;

LIN, X ;

WANG, Y ;

WANG, XK ;

YEE, A ;

KETTERSON, JB ;

CHANG, RPH .

SCIENCE, 1993, 259 (5101) :1601-1604

[4] Electrical conductivity of individual carbon nanotubes [J].

Ebbesen, TW ;

Lezec, HJ ;

Hiura, H ;

Bennett, JW ;

Ghaemi, HF ;

Thio, T .

NATURE, 1996, 382 (6586) :54-56

[5] PYROLYTIC CARBON NANOTUBES FROM VAPOR-GROWN CARBON-FIBERS [J].

ENDO, M ;

TAKEUCHI, K ;

KOBORI, K ;

TAKAHASHI, K ;

KROTO, HW ;

SARKAR, A .

CARBON, 1995, 33 (07) :873-881

[6] Fe-catalyzed carbon nanotube formation [J].

Hernadi, K ;

Fonseca, A ;

Nagy, JB ;

Bernaerts, D ;

Lucas, AA .

CARBON, 1996, 34 (10) :1249-1257

[7] MECHANICAL ALLOYING AND MILLING [J].

HERR, U .

NONEQUILIBRIUM MATERIALS, 1995, 103 :113-123

[8] HELICAL MICROTUBULES OF GRAPHITIC CARBON [J].

IIJIMA, S .

NATURE, 1991, 354 (6348) :56-58

[9] CARBON SPHERIC NANOPARTICLES - POSSIBLE FORMATION MECHANISM [J].

LOZOVIK, YE ;

POPOV, AM .

PHYSICS LETTERS A, 1994, 189 (1-2) :127-130

[10] HIGH-RESOLUTION ELECTRON-MICROSCOPY STUDIES IN CARBON SOOTS [J].

MIKIYOSHIDA, M ;

CASTILLO, R ;

RAMOS, S ;

RENDON, L ;

TEHUACANERO, S .

CARBON, 1994, 32 (02) :231-246