Susceptibility to pitting corrosion of 6056 aluminium alloy

被引：84

作者：

Blanc, C

Mankowski, G

机构：

[1] Laboratoire des Matériaux, ESA CNRS 5071, Ecl. Natl. Sup. de Chimie, 31077, Toulouse Cedex 4

来源：

CORROSION SCIENCE | 1997年 / 39卷 / 05期

关键词：

aluminium; copper; precipitates; pitting corrosion; chloride;

D O I：

10.1016/S0010-938X(97)81160-2

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The susceptibility to pitting corrosion of the 6056 alloy was studied and compared to that of the 2024 alloy. The 6056 alloy was more resistant to pitting than the 2024 alloy for high choride ion concentrations but less resistant for low chloride. Moreover, the variation of the susceptibility to pitting of the 6056 alloy with the potential was similar to that of pure aluminium, unlike the 2024 alloy which presented a peak of susceptibility to pitting. This difference was related to the behaviour of the coarse particles in the alloys. Because of this, the 6056 alloy appears more suitable than the 2024 alloy in conditions where pits can appear. (C) 1997 Elsevier Science Ltd.

引用

页码：949 / 959

页数：11

共 17 条

[1] AC-IMPEDANCE MEASUREMENTS ON ALUMINUM BARRIER TYPE OXIDE-FILMS [J].

BESSONE, J ;

MAYER, C ;

JUTTNER, K ;

LORENZ, WJ .

ELECTROCHIMICA ACTA, 1983, 28 (02) :171-175

[2]

BLANC C, IN PRESS CORROSION S

[3]

BURLEIGH TD, 1992, 3 INT C AL ALL TROND, P435

[4]

EDWARDS GA, 1994, P 4 INT C AL ALL ATL, V1, P620

[5] STRUCTURE OF METASTABLE PRECIPITATES FORMED DURING AGING OF AN AL-MG-SI ALLOY [J].

JACOBS, MH .

PHILOSOPHICAL MAGAZINE, 1972, 26 (01) :1-&

[6] MICROANALYSIS OF AGE-HARDENING PRECIPITATES IN ALUMINUM-ALLOYS [J].

LYNCH, JP ;

BROWN, LM ;

JACOBS, MH .

ACTA METALLURGICA, 1982, 30 (07) :1389-1395

[7]

Mankowski G., 1989, MATER SCI FORUM, V44-45, P279

[8]

MAZURKIEWICZ B, 1983, CORROS SCI, V23, P687, DOI 10.1016/0010-938X(83)90033-1

[9] MECHANISM OF PITTING OF ALUMINUM [J].

NGUYEN, TH ;

FOLEY, RT .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1979, 126 (11) :1855-1860

[10]

Nisancioglu K., 1993, Journal of Japan Institute of Light Metals, V43, P319, DOI 10.2464/jilm.43.319

← 1 2 →