Electrophoretic deposition for fabrication of YSZ electrolyte film on non-conducting porous NiO-YSZ composite substrate for intermediate temperature SOFC

Electrophoretic deposition (EPD) of YSZ electrolyte films onto porous NiO-YSZ composite substrates that had been pre-coated with graphite thin layers was carried out in the following two means for solid oxide fuel cell application: one was EPD based on electrophoretic filtration by which YSZ films were formed on the reverse sides without the graphite layers; the other was EPD on a graphite thin layer pre-coated on the substrates. Dense YSZ electrolyte thin films were successfully obtained in both means, although it was difficult to form YSZ films that were strongly adherent to the substrates using the latter means. The densification of YSZ films was assisted by shrinkage of the substrates during co-firing. A single cell was constructed on ca. 5 mu m thick dense YSZ films fabricated using the EPD based on electrophoretic filtration. Maximum power densities over 0.06, 0.35, 1. 0 and 2.01 W/cm(2) were attained, respectively, at 500, 600, 700 and 800 degrees C on the cell. (c) 2006 Elsevier Ltd. All rights reserved.