Performance tests of Bi-2212 insert magnets fabricated by Ag sheath method and dip-coating method

被引：8

作者：

Kumakura, H

Kitaguchi, H

Kiyoshi, T

Inoue, K

Togano, K

Okada, M

Fukushima, K

Tanaka, K

Kato, K

Sato, J

机构：

[1] HITACHI LTD,HITACHI RES LAB,HITACHI,IBARAKI 31912,JAPAN

[2] HITACHI CABLE LTD,TSUCHIURA,IBARAKI 300,JAPAN

来源：

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY | 1997年 / 7卷 / 02期

关键词：

D O I：

10.1109/77.614587

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

We have fabricated small magnets using Bi-2212/Ag tapes prepared by the combination of a powder-in-tube method or a dip-coating method and a wind-&-react method. The magnets were inserted in a 21 T superconducting magnet and tested under various bias fields at 4.2 K. All of the magnets could sustain large electromagnetic force under high magnetic fields, and no damage was introduced during the test. Critical current density of a magnet consisting of 4 double pancake coils was 9.5x10(4)A/cm(2) in 21 T which corresponded to the central generated field of 1.76 T. Thus the total field of 22.76 T was attained in a full superconducting state. No degradation of superconducting properties was produced by a thermal cycle and moisture in air.

引用

页码：646 / 649

页数：4

共 14 条

[1] RECENT ISSUES IN FABRICATION OF HIGH-TC MAGNETS AND LONG-LENGTH MULTIFILAMENT CONDUCTORS [J].

BALACHANDRAN, U ;

IYER, AN ;

HALDAR, P ;

HOEHN, JG ;

MOTOWIDLO, LR ;

GALINSKI, G .

APPLIED SUPERCONDUCTIVITY, 1994, 2 (3-4) :251-259

[2] PREPARATION OF THE TEXTURED BI-BASED OXIDE TAPES BY PARTIAL MELTING PROCESS [J].

KASE, J ;

MORIMOTO, T ;

TOGANO, K ;

KUMAKURA, H ;

DIETDERICH, DR ;

MAEDA, H .

IEEE TRANSACTIONS ON MAGNETICS, 1991, 27 (02) :1254-1257

[3]

KIYOSHI T, 1994, IEEE T MAGN, V30

[4]

KUMAKURA H, IN PRESS ADV CRYOGEN, V42

[5]

LUE JW, 1994, ADV CRYOG ENG, V40, P327

[6] Bi-2211/Ag superconducting insert magnet for high magnetic field generation over 22T [J].

Okada, M ;

Tanaka, K ;

Fukushima, K ;

Sato, J ;

Kitaguchi, H ;

Kumakura, H ;

Kiyoshi, T ;

Inoue, K ;

Togano, K .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1996, 35 (5B) :L623-L626

[7] TRANSPORT-PROPERTIES OF BI-2212/AG SUPERCONDUCTING MAGNET WITH I-C OVER 500 A [J].

OKADA, M ;

TANAKA, K ;

INOUE, N ;

SATO, J ;

KITAGUCHI, H ;

KUMAKURA, H ;

KIYOSI, T ;

INOUE, K ;

TOGANO, K .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1995, 34 (8A) :L981-L983

[8] FABRICATION OF SILVER-SHEATHED BI(2/2/1/2) SUPERCONDUCTING MAGNET BY MEANS OF PARTIAL MELT AND SLOW COOLING PROCESS [J].

SHIBUTANI, K ;

HASE, T ;

EGI, T ;

HAYASHI, S ;

OGAWA, R ;

KAWATE, Y .

APPLIED SUPERCONDUCTIVITY, 1994, 2 (3-4) :237-250

[9]

TENBRINK J, 1994, ADV CRYOG ENG, V40, P305

[10]

TOGANO K, 1992, ADV CRYOG ENG, V38, P1081

← 1 2 →