Mechanochemical synthesis of anatase and rutile nanopowders from TiOSO4

被引：41

作者：

Billik, P. ^{[1
]}

Plesch, G. ^{[1
]}

机构：

[1] Comenius Univ Mlynska Dolina, Fac Nat Sci, Dept Inorgan Chem, Bratislava 84215, Slovakia

来源：

MATERIALS LETTERS | 2007年 / 61卷 / 4-5期

关键词：

mcchanochemical synthesis; TiO2; anatase; rutile; nanomaterials;

D O I：

10.1016/j.matlet.2006.06.080

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The synthesis of titanium dioxide phases rutile and anatase via mechanochemical reaction and subsequent annealing of the products was studied. TiOSO4-xH(2)O and anhydrous Na2CO3 Powders in the molar ratio 1: 1 were used as starting reactants. The Na2SO4-xH(2)O by-product was removed by simple water washing process. The synthesis of nanocrystalline rutile is almost complete after 60 min milling and particles with average size of 15 nm were obtained. Nanoparticles of anatase with average size of 5-35 nm were obtained after 5 min milling and subsequent annealing at 300-600 degrees C. (c) 2006 Elsevier B.V All rights reserved.

引用

页码：1183 / 1186

页数：4

共 24 条

[1] Visible-light photocatalysis in nitrogen-doped titanium oxides [J].

Asahi, R ;

Morikawa, T ;

Ohwaki, T ;

Aoki, K ;

Taga, Y .

SCIENCE, 2001, 293 (5528) :269-271

[2]

Avvakumov E., 2001, SOFT MECHANOCHEMICAL, P2

[3] Mechanochemical route for sulphide nanoparticles preparation [J].

Baláz, P ;

Boldizárová, E ;

Godocíková, E ;

Briacin, J .

MATERIALS LETTERS, 2003, 57 (9-10) :1585-1589

[4] Kinetics and mechanisms of phase transformations induced by ball-milling in anatase TiO2 [J].

Bégin-Colin, S ;

Girot, T ;

Le Caër, G ;

Mocellin, A .

JOURNAL OF SOLID STATE CHEMISTRY, 2000, 149 (01) :41-48

[5] Hydrothermal reactions under mechanochemical action [J].

Boldyrev, VV .

POWDER TECHNOLOGY, 2002, 122 (2-3) :247-254

[6]

BREZOVA V, 2006, UNPUB P C ENV APPL A

[7] Syntheses of TiO2 photocatalysts by the molten salts method application to the photocatalytic degradation of Prosulfuron® [J].

Docters, T ;

Chovelon, JM ;

Herrmann, JM ;

Deloume, JP .

APPLIED CATALYSIS B-ENVIRONMENTAL, 2004, 50 (04) :219-226

[8] Nanocrystalline zirconia powders synthesised by mechanochemical processing [J].

Dodd, AC ;

Tsuzuki, T ;

McCormick, PG .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 301 (01) :54-58

[9] LIGHT-INDUCED REDOX REACTIONS IN NANOCRYSTALLINE SYSTEMS [J].

HAGFELDT, A ;

GRATZEL, M .

CHEMICAL REVIEWS, 1995, 95 (01) :49-68

[10] Modification of the physicochemical properties of commercial TiO2 samples by soft mechanical activation [J].

Hidalgo, MC ;

Colón, G ;

Navío, JA .

JOURNAL OF PHOTOCHEMISTRY AND PHOTOBIOLOGY A-CHEMISTRY, 2002, 148 (1-3) :341-348

← 1 2 3 →