Impact essential work of fracture of polypropylene/montmorillonite nanocomposites toughened with SEBS-g-MA elastomer

被引：83

作者：

Bao, S. P. ^{[1
]}

Tjong, S. C. ^{[1
]}

机构：

[1] City Univ Hong Kong, Dept Phys & Mat Sci, Kowloon, Hong Kong, Peoples R China

来源：

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING | 2007年 / 38卷 / 02期

关键词：

nano-structures; fracture toughness; impact behavior; injection moulding;

D O I：

10.1016/j.compositesa.2006.03.005

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Poly(propylene) (PP)/organo-montmorillonite (Org-MMT) nanocomposites toughened with maleated styrene-ethylene-butylene-sty.rene (SEBS-g-MA) were prepared via melt compounding. X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to evaluate the effects of the Org-MMT and SEBS-g-MA additions on the structure of nanocomposites. XRD traces showed that the characteristic (00 1) peak of the nanocomposites shifted to the lower angle region. Multi-layered stacks of clay platelets and independent exfoliated platelets were observed in TEM image. This implied that mixed intercalated and exfoliated structure were developed in the nanocomposites. The impact essential work of fracture (EWF) tests were used to evaluate the impact fracture toughness of the nanocomposites toughened with elastomer. The results showed that the SEBS-g-MA additions were beneficial in enhancing the essential and non-essential work of fracture of the nanocomposites. (c) 2006 Elsevier Ltd. All rights reserved.

引用

页码：378 / 387

页数：10

共 53 条

[1]

[Anonymous], 1995, POLYPROPYLENE STRUCT

[2] PHASE-TRANSITION FROM A C-CENTERED TO A B-CENTERED ORTHORHOMBIC CRYSTALLINE FORM OF SYNDIOTACTIC POLY(PROPYLENE) [J].

AURIEMMA, F ;

LEWIS, RH ;

SPIESS, HW ;

DEROSA, C .

MACROMOLECULAR CHEMISTRY AND PHYSICS, 1995, 196 (12) :4011-4024

[3] HETEROGENEOUS NUCLEATION IN CRYSTALLIZATION OF POLYOLEFINS .1. CHEMICAL AND PHYSICAL NATURE OF NUCLEATING AGENTS [J].

BINSBERG.FL .

POLYMER, 1970, 11 (05) :253-&

[4] MECHANICAL MOTIONS IN AMORPHOUS AND SEMI-CRYSTALLINE POLYMERS [J].

BOYER, RF .

POLYMER, 1976, 17 (11) :996-1008

[5] Polypropylene/calcium carbonate nanocomposites [J].

Chan, CM ;

Wu, JS ;

Li, JX ;

Cheung, YK .

POLYMER, 2002, 43 (10) :2981-2992

[6] Comparison of nanocomposites based on nylon 6 and nylon 66 [J].

Chavarria, F ;

Paul, DR .

POLYMER, 2004, 45 (25) :8501-8515

[7] Impact specific essential work of fracture of compatibilized polyamide-6 (PA6)/poly(phenylene ether) (PPE) blends [J].

Chiou, KC ;

Chang, FC ;

Mai, YW .

POLYMER ENGINEERING AND SCIENCE, 2001, 41 (06) :1007-1018

[8] Combined effects of clay modifications and compatibilizers on the formation and physical properties of melt-mixed polypropylene/clay nanocomposites [J].

Chiu, FC ;

Lai, SM ;

Chen, JW ;

Chu, PH .

JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 2004, 42 (22) :4139-4150

[9] Polypropylene/talc/SEBS (SEBS-g-MA) composites. Part 2. Mechanical properties [J].

Denac, M ;

Musil, V ;

Smit, I .

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2005, 36 (09) :1282-1290

[10]

Denac M., 2001, MATER TECHNOL, V35, P243

← 1 2 3 4 5 6 →