Polyol process synthesis of monodispersed FePt nanoparticles

被引：133

作者：

Liu, C ^{[1
]}

Wu, XW

Klemmer, T

Shukla, N

Yang, XM

Weller, D

Roy, AG

Tanase, M

Laughlin, D

机构：

[1] Seagate Res, Pittsburgh, PA 15222 USA

[2] Carnegie Mellon Univ, Ctr Data Storage Syst, Pittsburgh, PA 15213 USA

来源：

JOURNAL OF PHYSICAL CHEMISTRY B | 2004年 / 108卷 / 20期

关键词：

D O I：

10.1021/jp0312971

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Monodispersed FePt nanoparticles are synthesized by reduction of iron(II) acetylacetonate and platinum(II) acetylacetonate with 1,2-hexadecanediol as the reducing reagent in the polyol process. As-prepared FePt nanoparticles are chemically disordered with fcc phase. Transmission electron microscopy (TEM) images show a self-assembled particle array with an average particle size of 3 nm and a standard deviation about 10%. The transformation from chemically disordered fcc to chemically ordered Ll(0) phase is achieved by annealing at 650 degreesC for 30 min in Ar atmosphere where the oxygen level is less than 1 ppm. Magnetic hysteresis measurements show a coercivity of 9.0 kOe at 293 K, and 16.7 kOe at 5 K for the annealed FePt nanoparticles.

引用

收藏

页码：6121 / 6123

页数：3

相关论文

共 12 条

[1] Polyol-process-derived CoPt nanoparticles: Structural and magnetic properties [J].

Chinnasamy, CN ;

Jeyadevan, B ;

Shinoda, K ;

Tohji, K .

JOURNAL OF APPLIED PHYSICS, 2003, 93 (10) :7583-7585

[2] Phase transformation, coalescence, and twinning of monodisperse FePt nanocrystals [J].

Dai, ZR ;

Sun, SH ;

Wang, ZL .

NANO LETTERS, 2001, 1 (08) :443-447

[3] Shapes, multiple twins and surface structures of monodisperse FePt magnetic nanocrystals [J].

Dai, ZR ;

Sun, SH ;

Wang, ZL .

SURFACE SCIENCE, 2002, 505 (1-3) :325-335

[4] Direct synthesis of fct-FePt nanoparticles by chemical route [J].

Jeyadevan, B ;

Urakawa, K ;

Hobo, A ;

Chinnasamy, N ;

Shinoda, K ;

Tohji, K ;

Djayaprawira, DDJ ;

Tsunoda, M ;

Takahashi, M .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 2003, 42 (4A) :L350-L352

[5] Towards direct synthesis of fct-FePt nanoparticles by chemical route [J].

Jeyadevan, B ;

Hobo, A ;

Urakawa, K ;

Chinnasamy, CN ;

Shinoda, K ;

Tohji, K .

JOURNAL OF APPLIED PHYSICS, 2003, 93 (10) :7574-7576

[6]

Sun S., 2001, Journal of the Magnetics Society of Japan, V25, P1434

[7] Size-controlled synthesis of magnetite nanoparticles [J].

Sun, SH ;

Zeng, H .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2002, 124 (28) :8204-8205

[8] Controlled synthesis and assembly of FePt nanoparticles [J].

Sun, SH ;

Anders, S ;

Thomson, T ;

Baglin, JEE ;

Toney, MF ;

Hamann, HF ;

Murray, CB ;

Terris, BD .

JOURNAL OF PHYSICAL CHEMISTRY B, 2003, 107 (23) :5419-5425

[9] Monodisperse FePt nanoparticles and ferromagnetic FePt nanocrystal superlattices [J].

Sun, SH ;

Murray, CB ;

Weller, D ;

Folks, L ;

Moser, A .

SCIENCE, 2000, 287 (5460) :1989-1992

[10] Monodisperse iron-based particles: Precipitation in liquid polyols [J].

Viau, G ;

FievetVincent, F ;

Fievet, F .

JOURNAL OF MATERIALS CHEMISTRY, 1996, 6 (06) :1047-1053