CFRP strengthened butt-welded very high strength (VHS) circular steel tubes

被引：144

作者：

Jiao, H ^{[1
]}

Zhao, XL ^{[1
]}

机构：

[1] Monash Univ, Dept Civil Engn, Clayton, Vic 3168, Australia

来源：

THIN-WALLED STRUCTURES | 2004年 / 42卷 / 07期

基金：

澳大利亚研究理事会;

关键词：

carbon fibre reinforced plastics; high strength steel; tubes; welding; tension;

D O I：

10.1016/j.tws.2004.03.003

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

This paper investigates the behavior of carbon fibre reinforced plastics (CFRP) strengthened butt-welded very high strength (VHS) circular steel tubes. The VHS steel has a yield stress of 1350 MPa and an ultimate strength of 1500 MPa. Three types of epoxy resins with different lap shear strength were used. Tests were conducted to determine the lap shear strength between CFRP and VHS steel tubes. A total of 21 butt-welded VHS tubes strengthened with CFRP were tested in axial tension. Three kinds of failure modes, i.e. adhesive failure, fiber tear and mixed failure were observed. The suitable epoxy adhesive for strengthening VHS tubes was recommended. A significant strength increase was achieved using CFRP-epoxy strengthening technique. A theoretical model was developed to estimate the load carrying capacity of butt-welded VHS tubes strengthened using CFRP. (C) 2004 Elsevier Ltd. All rights reserved.

引用

页码：963 / 978

页数：16

共 26 条

[1]

AKSELSEN OM, 1989, WELD J, V68, pS356

[2]

*ASTM, 1999, 5573 ASTM, P476

[3]

*ASTM, 1999, 589601 ASTM, P424

[4]

*ASTM, 2001, 586801 ASTM, P518

[5]

Bassetti A, 1998, VTT SYMP, V182, P535

[6]

Cederquist SC, 1999, MATER PERFORMANCE, V38, P20

[7]

*CIB ADH, 2000, SURF PREP PRETR STRU, P136

[8]

CULLISON A, 1995, WELDING J, V74

[9] Material ductility of very high strength (VHS) circular steel tubes in tension [J].

Jiao, H ;

Zhao, XL .

THIN-WALLED STRUCTURES, 2001, 39 (11) :887-906

[10]

JIAO H, 2004, IN PRESS THIN WALLED

← 1 2 3 →