Oxidation of 310 steel in H2O/O2 mixtures at 600 °C:: the effect of water-vapour-enhanced chromium evaporation

被引：130

作者：

Asteman, H ^{[1
]}

Svensson, JE

Johansson, LG

机构：

[1] Gothenburg Univ, Dept Chem, S-41296 Gothenburg, Sweden

[2] Chalmers Univ Technol, Dept Environm Inorgan Chem, S-41296 Gothenburg, Sweden

来源：

CORROSION SCIENCE | 2002年 / 44卷 / 11期

关键词：

stainless steel; AES; SEM; high temperature corrosion; selective oxidation;

D O I：

10.1016/S0010-938X(02)00056-2

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The oxidation of type 310 stainless steel was investigated at 600 degreesC in the presence of O-2 and O-2 + 10% and 40% H2O. The effect of gas velocity was studied. The oxidized samples were investigated by grazing angle X-ray diffraction, SEM/EDX and SAM. The addition of H2O to O-2 resulted in a change of oxidation behaviour. A strong dependence on flow rate was observed in O-2/H2O mixtures. At low flow rates a thin (30-50 nm) protective alpha-(Cr,Fe)(2)O-3 formed, the outer part being depleted in chromium. When the flow rate was increased beyond a critical value the protective oxide failed. Under these conditions greater than or equal to 5 mum thick alpha-Fe2O3/(Cr,Fe)(3)O-4, oxide islands formed on the part of the surface corresponding to the centre of the alloy grains. The effect of water vapour is attributed to the water-vapour-assisted evaporation of chromium from the oxide, in the form of a chromium oxide hydroxide, probably CrO2(OH)(2). The oxidation behaviour is rationalized using a qualitative mechanism proposed previously and parallels that of the 304L alloy. (C) 2002 Published by Elsevier Science Ltd.

引用

页码：2635 / 2649

页数：15

共 16 条

[1]

AMY S, 2001, P EUR 2001 SEPT 30 R

[2] Evidence for chromium evaporation influencing the oxidation of 304L: The effect of temperature and flow rate [J].

Asteman, H ;

Svensson, JE ;

Johansson, LG .

OXIDATION OF METALS, 2002, 57 (3-4) :193-216

[3] Influence of water vapor and flow rate on the high-temperature oxidation of 304L; Effect of chromium oxide hydroxide evaporation [J].

Asteman, H ;

Svensson, JE ;

Norell, M ;

Johansson, LG .

OXIDATION OF METALS, 2000, 54 (1-2) :11-26

[4] Indication of chromium oxide hydroxide evaporation during oxidation of 304L at 873 K in the presence of 10% water vapor [J].

Asteman, H ;

Svensson, JE ;

Johansson, LG ;

Norell, M .

OXIDATION OF METALS, 1999, 52 (1-2) :95-111

[5]

ASTEMAN H, IN PRESS SIA

[6] THE VOLATILIZATION OF CHROMIUM OXIDE [J].

CAPLAN, D ;

COHEN, M .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1961, 108 (05) :438-442

[7] THE MECHANISM OF THE HIGH-TEMPERATURE OXIDATION OF IRON-CHROMIUM ALLOYS IN WATER VAPOR [J].

FUJII, CT ;

MEUSSNER, RA .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1964, 111 (11) :1215-1221

[8] Abnormal oxidation of stabilized ferritic stainless steels in water vapor [J].

Henry, S ;

Galerie, A ;

Antoni, L .

HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2, 2001, 369-3 :353-360

[9] ELECTRICAL-CONDUCTIVITY AND DEFECT STRUCTURE OF CR2O3 .2. REDUCED TEMPERATURES (LESS-THAN-SIMILAR-TO-1000-DEGREES-C) [J].

HOLT, A ;

KOFSTAD, P .

SOLID STATE IONICS, 1994, 69 (02) :137-143

[10]

JIANIAN S, 1997, OXID MET, V48, P347

← 1 2 →