Uniform titanium dioxide (TiO2) microcapsules prepared by glass membrane emulsification with subsequent solvent evaporation

被引:21
作者
Supsakulchai, A [1 ]
Ma, GH [1 ]
Nagai, M [1 ]
Omi, S [1 ]
机构
[1] Tokyo Univ Agr & Technol, Grad Sch Bioapplicat & Syst Engn, Tokyo 1848588, Japan
关键词
titanium dioxide microcapsules; porous glass (SPG) membrane; solvent evaporation; styrene copolymers;
D O I
10.1080/02652040210142542
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
Anatase-type titanium dioxide (TiO2) was encapsulated using an Shirasu porous glass (SPG) membrane emulsification technique and followed by solvent evaporation. The oil phase, consisting of fine powder of anatase TiO2, Disperbyk-180, the hydrophobic oil phase additive, and polymer wall solution, was pushed through the membrane pores into the aqueous phase of poly( vinyl alcohol) and sodium dodecyl sulfate to form the solid-in-oil-in water, (S/O)/W, emulsion droplets. Three types of styrene-based copolymer poly( styrene-co-acrylic acid) (PS-AA), poly( styrene-co-2-ethyl hexyl acrylate) (PS-2EHA) and poly( styrene-co-dimethyl aminoethylmethacrylate) (PS-DMAEMA) were used as an encapsulating shell. Uniform droplets were successfully obtained by modifying the oil phase using methyl laurate or hexadecanol as the oil phase additive, together with carefully monitoring the emulsification flow rate during the emulsification. The (S/O)/W emulsion was gently stirred in a sealed reactor, and evacuation of solvent started under moderate heating with increasing a vacuum intensity. Those uniform-sized TiO2 microcapsules revealed fine porous morphologies on their surfaces as a result of a mild phase separation induced from the addition of the oil phase additive. The encapsulation efficiency was influenced by the stability of TiO2 in the oil phase, the polymer wall employed, and the operational control of the glass membrane emulsification process. The membrane emulsification process could prepare the TiO2 microcapsules with about similar to6-8.5 wt% of encapsulation loadings. PS-AA and PS-2EHA copolymers provided better encapsulation efficiency compared to PS-DMAEMA. SPG membranes with 1.42, 2.8, 5.25, 7.0, or 9.5 mum were employed and 2-20 mum microcapsules were subsequently obtained.
引用
收藏
页码:425 / 449
页数:25
相关论文
共 28 条
[1]  
[Anonymous], 1991, MEMBRANE EMULSIFICAT
[2]  
BRANDRUP H, 1997, POLYM HDB, P519
[3]   POLYMERIZATION OF MMA AT THE SURFACE OF INORGANIC SUB-MICRON PARTICLES [J].
CARIS, CHM ;
VANELVEN, LPM ;
VANHERK, AM ;
GERMAN, AL .
BRITISH POLYMER JOURNAL, 1989, 21 (02) :133-140
[4]   KINETICS OF (CO)POLYMERIZATIONS AT THE SURFACE OF INORGANIC SUBMICRON PARTICLES IN EMULSION-LIKE SYSTEMS [J].
CARIS, CHM ;
KUIJPERS, RPM ;
VANHERK, AM ;
GERMAN, AL .
MAKROMOLEKULARE CHEMIE-MACROMOLECULAR SYMPOSIA, 1990, 35-6 :535-548
[5]  
Erdem B, 2000, J POLYM SCI POL CHEM, V38, P4431, DOI 10.1002/1099-0518(20001215)38:24<4431::AID-POLA120>3.0.CO
[6]  
2-Y
[7]  
Erdem B, 2000, J POLYM SCI POL CHEM, V38, P4441, DOI 10.1002/1099-0518(20001215)38:24<4441::AID-POLA130>3.0.CO
[8]  
2-U
[9]   PHYSICAL DEGRADATION OF EMULSIONS VIA MOLECULAR DIFFUSION ROUTE AND POSSIBLE PREVENTION THEREOF [J].
HIGUCHI, WI ;
MISRA, J .
JOURNAL OF PHARMACEUTICAL SCIENCES, 1962, 51 (05) :459-&
[10]   HETEROGENEOUS PHOTOCATALYSIS - DEGRADATION OF DILUTE-SOLUTIONS OF DICHLOROMETHANE (CH2CL2), CHLOROFORM (CHCL3), AND CARBON-TETRACHLORIDE (CCL4) WITH ILLUMINATED TIO2 PHOTOCATALYST [J].
HSIAO, CY ;
LEE, CL ;
OLLIS, DF .
JOURNAL OF CATALYSIS, 1983, 82 (02) :418-423