Tribological behaviour of borided bearing steels at elevated temperatures

Borided steels are known to exhibit excellent wear resistance at room temperature. However, the sliding wear behaviour of borided steels at high temperatures is not known. In the present study, AISI 440C and 52100 bearing steels which are extensively used in industry, were borided by pack method at 950 degrees C for 2 h. X-ray diffraction analysis of boride layers on the surface of steels revealed various peaks of FeB, Fe2B and CrB. The thickness and hardness of boride layers on the 52100 and 440C steels were 56 +/- 6 and 47 +/- 4 mu m and 1970 and 2160 HK, respectively. Dry sliding wear tests of these borided steels were performed against Si3N4 bearing ball at a constant sliding speed and load at elevated temperatures. The temperature changed between room temperature and 600 degrees C. These tests indicated that the wear rates of unborided and borided steels increase with temperature and borided 52 100 and 440C steels exhibit considerably lower wear rate at all temperatures, compared with unborided steels. At temperature of 600 degrees C, borided 52100 and 440C steels have a wear resistance of about 3 and 2.5 times higher than that of unborided steels, respectively. Examination of the worn surface of borided steels showed that, worn surfaces were covered with a discontinuous compact layer especially above temperature of 300 degrees C. (c) 2006 Published by Elsevier B.V.