Kinetics and mechanism of formation of monocalcium aluminate, CaAl2O4

被引：58

作者：

Mohamed, BM

Sharp, JH

机构：

[1] Department of Engineering Materials, University of Sheffield, Sheffield S1 3JD, Mappin Street

来源：

JOURNAL OF MATERIALS CHEMISTRY | 1997年 / 7卷 / 08期

关键词：

D O I：

10.1039/a700201g

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The kinetics of the reaction for the formation of monocalcium aluminate (CaAl2O4) using 1 : 1 molar mixtures of A.R. grade calcium carbonate and A.R. alpha-Al2O3 Or gibbsite have been investigated in the range 1150-1400 degrees C using quantitative X-ray diffraction analysis. The phases Ca3Al2O6 and Ca12Al14O33 were found to be intermediates in the formation of CaAl2O4, whereas CaAl4O7 was formed via an initial side reaction. The formation of CaAl2O4 from the oxides was found to fit well with the diffusion controlled model of Ginstling and Brounshtein. The activation energy for the formation of CaAl2O4 from the amount of CaAl2O4 formed from the reaction of calcite with alpha-Al2O3 was determined to be 205 +/- 10 kJ mol(-1).

引用

页码：1595 / 1599

页数：5

共 16 条

[1]

[Anonymous], 1983, LONDON APPL SCI

[2]

AYRAMI M, 1941, J CHEM PHYS, V9, P177

[3] FLEXURAL STRENGTH AND POROSITY OF CEMENTS [J].