Examination of fracture surfaces using focused ion beam milling

被引：23

作者：

Cairney, JM ^{[1
]}

Munroe, PR

Schneibel, JH

机构：

[1] Univ New S Wales, Sydney, NSW 2052, Australia

[2] Oak Ridge Natl Lab, Div Met & Ceram, Oak Ridge, TN 37831 USA

来源：

SCRIPTA MATERIALIA | 2000年 / 42卷 / 05期

关键词：

composites; intermetallic; fracture;

D O I：

10.1016/S1359-6462(99)00374-7

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

For the purposes of iron analysis, the focused ion beam was used to obtain cross-sections of fracture surfaces in FeAl-WC and FeAl-TiC composites. On comparing debonded regions of the two composites, a greater extent of debonding was observed in FeAl-TiC, on the order of the particle size. The FeAl-WC exhibited less debonding, and a greater degree of plastic deformation in the matrix. These results suggest weaker interfacial bonding in the FeAl-TiC.

引用

页码：473 / 478

页数：6

共 14 条

[1]

Baker I, 1997, INT MATER REV, V42, P181, DOI 10.1179/095066097790093190

[2] AN ENVIRONMENTAL-EFFECT AS THE MAJOR CAUSE FOR ROOM-TEMPERATURE EMBRITTLEMENT IN FEAL [J].

LIU, CT ;

LEE, EH ;

MCKAMEY, CG .

SCRIPTA METALLURGICA, 1989, 23 (06) :875-880

[3] FOCUSED ION-BEAM TECHNOLOGY AND APPLICATIONS [J].

MELNGAILIS, J .

JOURNAL OF VACUUM SCIENCE & TECHNOLOGY B, 1987, 5 (02) :469-495

[4] IDENTIFICATION OF THERMODYNAMICALLY STABLE CERAMIC REINFORCEMENT MATERIALS FOR IRON ALUMINIDE MATRICES [J].

MISRA, AK .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1990, 21 (02) :441-446

[5] APPLICATIONS OF FOCUSED ION-BEAM TECHNIQUE TO FAILURE ANALYSIS OF VERY LARGE-SCALE INTEGRATIONS - A REVIEW [J].

NIKAWA, K .

JOURNAL OF VACUUM SCIENCE & TECHNOLOGY B, 1991, 9 (05) :2566-2577

[6]

Phaneuf M. W., 1998, Microscopy and Microanalysis, V4, P492, DOI 10.1017/S1431927600022583

[7]

ROWLANDS N, IN PRESS INT MET S C

[8] Liquid-phase sintered iron aluminide-ceramic composites [J].

Schneibel, JH ;

Carmichael, CA ;

Specht, ED ;

Subramanian, R .

INTERMETALLICS, 1997, 5 (01) :61-67

[9]

SCHNEIBEL JH, 1994, PROCESSING PROPERTIE, P315

[10]

SCHNEIBEL JH, 1996, P INT S NICK IR AL P, P329

← 1 2 →