The solubility of C in solid Cu

被引：278

作者：

López, GA

Mittemeijer, E

机构：

[1] Univ Stuttgart, Max Planck Inst Met Res, D-70569 Stuttgart, Germany

[2] Univ Stuttgart, Inst Phys Met, D-70569 Stuttgart, Germany

来源：

SCRIPTA MATERIALIA | 2004年 / 51卷 / 01期

关键词：

solubility of C in solid Cu; Cu-C system; interstitial solid solutions; combustion analysis;

D O I：

10.1016/j.scriptamat.2004.03.028

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The solubility of C in solid Cu was determined in the temperature range 1143-1293 K. Layers of C were vapour deposited onto high-purity Cu slices, which were annealed for 72 and 240 h at different temperatures. The C content in the samples was determined by means of combustion analysis. A Henrian behaviour for the carbon activity in the interstitial solid solution was observed. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

引用

页码：1 / 5

页数：5

共 11 条

[1] BEVER MB, 1946, T AM I MIN MET ENG, V166, P128
[2] Diffusivity of carbon in the copper matrix. Influence of alloying
Dorfman, S
Fuks, D
[J]. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 1996, 27 (09) : 697 - 701
[3] Stability of copper segregations on copper/carbon metal-matrix composite interfaces under alloying
Dorfman, S
Fuks, D
[J]. COMPOSITES SCIENCE AND TECHNOLOGY, 1997, 57 (08) : 1065 - 1069
[4] A MODIFIED COMBUSTION METHOD FOR THE DETERMINATION OF THE SURFACE AND BULK CARBON CONTENTS OF HIGH-PURITY METALS
GRETZINGER, K
GRALLATH, E
TOLG, G
[J]. ANALYTICA CHIMICA ACTA, 1987, 193 : 1 - 18
[5] IMPROVEMENTS IN THE COMBUSTION METHOD FOR THE DETERMINATION OF LOW-CARBON CONTENTS IN STEEL
GRUNER, W
GRALLATH, E
[J]. STEEL RESEARCH, 1995, 66 (11): : 455 - 457
[6] LECLAIRE AD, 1990, DIFFUSION SOLID META, V26, P498
[7] SOLUBILITY OF CARBON IN SILVER, COPPER AND GOLD
MATHIEU, G
GUIOT, S
CABANE, J
[J]. SCRIPTA METALLURGICA, 1973, 7 (04): : 421 - 425
[8] SOLUBILITY OF CARBON IN SOLID GOLD COPPER AND SILVER
MCLELLAN, RB
[J]. SCRIPTA METALLURGICA, 1969, 3 (06): : 389 - &
[9] MCLELLAN RB, 1966, PHASE STABILITY META, P398
[10] CU-C AND AL-CU-C PHASE-DIAGRAMS AND THERMODYNAMIC PROPERTIES OF C IN THE ALLOYS FROM 1550-DEGREES-C TO 2300 DEGREES-C
ODEN, LL
GOKCEN, NA
[J]. METALLURGICAL TRANSACTIONS B-PROCESS METALLURGY, 1992, 23 (04): : 453 - 458

← 1 2 →