Preparation and thermornechanical properties of epoxy resins modified by octafunctional cubic silsesquioxane epoxides

被引:75
作者
Mya, KY
He, CB
Huang, JC
Xiao, Y
Dai, J
Siow, YP
机构
[1] Inst Mat Res & Engn, Singapore 117602, Singapore
[2] DSO Natl Labs, Singapore 118230, Singapore
关键词
additives; thermosets; WAXS; octafunctional cubic silsesquioxane epoxides; thermo properties; mechanical properties; polyhedral oligomeric silsesquioxane (POSS)-modified epoxy resins;
D O I
10.1002/pola.20168
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
The thermomechanical properties of octafunctional cubic silsesquioxane-modified epoxy resins associated with dicycloaliphatic hardener (4,4'-dimethyldiaminodicyclo hexyl methane) were studied using thermogravimetric analysis, differential scanning calorimetry, and dynamic mechanical analysis. The structures of epoxy resin containing cubic silsesquioxane epoxides were characterized by Fourier transform infrared spectroscopy and wide-angle X-ray scattering techniques. In this work, octa(dimethylsiloxybutylepoxide) octasilsesquioxane (OB), and octa(glycidyldimethylsiloxyepoxide) octasilsesquioxane (OG), were synthesized and used as additives to improve the properties of a commercial epoxy resin by exploring the effects of varying the ratio of OB or OG. The commercial Ciba epoxy resin (Araldite LY5210/HY2954) was used as a standard. It was found, by thermogravimetric analysis and dynamic mechanical analysis, that the highest thermal stability was observed at N = 0.5 (N = number of amine groups/number of epoxy rings). No glass transition temperature was observed by adding 20 mol % OB to the Ciba epoxy resin, indicating the reduction of chain motion in the presence of octafunctional cubic silsesquioxane epoxide. The storage modulus of the OB-modified epoxy resin also increased, especially at higher temperatures, compared with the Ciba epoxy resin under identical curing conditions. Fourier transform infrared data elucidated the preservation of cubic silsesquioxane structure after curing at high temperature. In contrast, the OG/Araldite LY5210/HY2954 systems gave poorer thermomechanical properties. The low viscosity of OB at room temperature (similar to 350 cPs) makes it suitable for composite processing and, when used in conjunction with the Ciba epoxy, lowers the viscosity of this system as well. (C) 2004 Wiley Periodicals, Inc.
引用
收藏
页码:3490 / 3503
页数:14
相关论文
共 40 条
[1]   NEW SYNTHETIC ROUTE TO THE HYDRIDOSPHEROSILOXANES OH-H8SI8O12 AND D5H-H10SI10O15 [J].
AGASKAR, PA .
INORGANIC CHEMISTRY, 1991, 30 (13) :2707-2708
[2]  
ATNA DJ, 2003, ADHESION SCI TECHNOL, V17, P1655
[3]  
*BRUK AXS INC, 1999, GEN AR DET DIFFR SYS
[4]   New liquid-crystal line thermosets from liquid-crystalline bisazomethynic epoxy resins with naphthylene disruptors in the central core [J].
Castell, P ;
Serra, A ;
Galià, M .
JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 2003, 41 (10) :1536-1544
[5]   Thermal properties of side-chain phosphorus-containing epoxide cured with amine [J].
Cheng, KC ;
Yu, SY ;
Chiu, WY .
JOURNAL OF APPLIED POLYMER SCIENCE, 2002, 83 (13) :2741-2748
[6]   Organic/inorganic hybrid composites from cubic silsesquioxanes [J].
Choi, J ;
Harcup, J ;
Yee, AF ;
Zhu, Q ;
Laine, RM .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2001, 123 (46) :11420-11430
[7]   Organic/inorganic imide nanocomposites from aminophenylsilsesquioxanes [J].
Choi, JW ;
Tamaki, R ;
Kim, SG ;
Laine, RM .
CHEMISTRY OF MATERIALS, 2003, 15 (17) :3365-3375
[8]  
Crivello JV, 1997, J POLYM SCI POL CHEM, V35, P407
[9]   Nanostructure toughened epoxy resins [J].
Dean, JM ;
Verghese, NE ;
Pham, HQ ;
Bates, FS .
MACROMOLECULES, 2003, 36 (25) :9267-9270
[10]  
Ellis B, 1993, CHEM TECHNOLOGY EPOX