Rehydration of Zn-Al layered double hydroxides

Rehydration is shown to be straightforward for the reconstruction of polyoxometallate-pillared layered double hydroxides. Zn-Al hydrotalcite-like minerals were prepared with Zn/Al ratios of 1 to 5 by coprecipitation at pH 7. Good crystallinity was obtained for samples with Zn/Al ratios above 2. Thermal decomposition was achieved by calcining the samples at 300 to 900 degrees C. The calcined samples were exposed to decarbonated water, with or without hydrothermal treatment to evaluate reconstruction of the hydrotalcite-like minerals by rehydration. Restoration of the hydrotalcite-like structure was found to be independent of the Zn/Al ratios for samples calcined between 300 and 400 degrees C; however a second phase, aluminum hydroxide or zinc oxide, was generally detected. A spinel phase, formed during the calcination of samples at temperatures above 600 degrees C, inhibited reconstruction of the hydrotalcite-like phase. The rehydrated hydrotalcite-like minerals had Zn/Al ratios close to 2, irrespective of the chemistry of the starting material.