Kinetic study of the infiltration of aluminum alloys into TiC preforms

被引：18

作者：

Contreras, A

Salazar, M

León, CA

Drew, RAL

Bedolla, E

机构：

[1] UMSNH, Inst Invest Met, Morelia, Michoacan, Mexico

[2] McGill Univ, Dept Met Engn, Montreal, PQ, Canada

来源：

MATERIALS AND MANUFACTURING PROCESSES | 2000年 / 15卷 / 02期

关键词：

D O I：

10.1080/10426910008912980

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A study of the infiltration process of several alloys (Al-2024, Al-6061, and Al-7075) into preforms of TiC was carried out. The preforms were sintered for one hour under argon at 1250, 1350, and 1450 degrees C with the aim of achieving different levels of densification. Using a thermogravimetric analyzer (TGA), infiltration profiles were obtained by continuously monitoring the weight change of preforms partially immersed in molten aluminum. Infiltration was carried out at different temperatures (ranging from 900 to 1200 degrees C) under argon to evaluate infiltration kinetics. The infiltration rate of the aluminum into the preforms followed parabolic behavior and the activation energy changed according to the extent of preform densification. Average activation energies of 74, 99, and 138 k J mol(-1) were obtained for the Al-7075, Al-6061, and Al-2024 alloys, respectively. Prior to infiltration, an incubation period was observed and its length depended on the temperature; lower the infiltration temperature, longer was the incubation period.

引用

页码：163 / 182

页数：20

共 22 条

[1]

ARAMBURO GP, 1996, 2 REUN INT MAT COMP, P169

[2] DEVELOPMENT OF AL-TI-C GRAIN REFINERS CONTAINING TIC [J].

BANERJI, A ;

REIF, W .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (12) :2127-2137

[3] WEAR MECHANISMS DURING LUBRICATED SLIDING OF XD(TM) 2024-AL/TIB2 METAL MATRIX COMPOSITES AGAINST STEEL [J].

CARACOSTAS, CA ;

CHIOU, WA ;

FINE, ME ;

CHENG, HS .

SCRIPTA METALLURGICA ET MATERIALIA, 1992, 27 (02) :167-172

[4]

Contreras A., 1997, INT MAT RES C CANC Q, P2

[5]

DIXON W, ITA SEM

[6] DISCUSSION OF ON THE FREE-ENERGY OF FORMATION OF TIC AND AL4C3 [J].

FINE, ME ;

CONLEY, JG .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1990, 21 (09) :2609-2610

[7]

GARCIA AH, 1996, 2 REUN INT MAT COMP, P130

[8] SURFACE-TENSION OF BINARY AND TERNARY ALUMINUM-ALLOYS OF THE SYSTEMS AL-SI-MG AND AL-ZN-MG [J].

GOICOECHEA, J ;

GARCIACORDOVILLA, C ;

LOUIS, E ;

PAMIES, A .

JOURNAL OF MATERIALS SCIENCE, 1992, 27 (19) :5247-5252

[9]

JHA AK, 1990, METAL & CERAMIC MATRIX COMPOSITES : PROCESSING MODELING & MECHANICAL BEHAVIOR, P127

[10] Effect of various processing methods on the interfacial reactions in SiCp 2024 Al composites [J].

Lee, JC ;

Byun, JY ;

Oh, CS ;

Seok, HK ;

Lee, HI .

ACTA MATERIALIA, 1997, 45 (12) :5303-5315

← 1 2 3 →