Water absorption of a diglycidyl ether of bisphenol A/1,3-bisaminomethylcyclohexane (DGEBA/1,3-BAC) epoxy resin system

The diffusive and dynamic mechanical behavior of the DGEBA/1,3-BAC epoxy resin system was studied during water absorption. The diffusion of water was investigated at 100% relative humidity, by immersion of specimens in water at 60, 80 and 100 degrees C. in all absorption experiments, water diffusion followed Fick's law. Diffusion coefficients and saturated water concentrations are given for these temperatures. The activation energy for diffusion was determined from the relationship between the diffusion coefficient and the reciprocal of the absolute temperature. The value obtained was 31.2 kJ mol(-1). Dynamic mechanical analysis of samples immersed in 100 degrees C water and with various water contents showed both a shift of T-g, defined by the tan delta peak, to lower temperatures and a slight decrease in the dynamic modulus in the presence of water. These effects are probably a result of plasticization.