Microwave sintering of calcium phosphate ceramics

被引：57

作者：

Chanda, Abhijit ^{[2
]}

Dasgupta, Sudip ^{[1
]}

Bose, Susmita ^{[1
]}

Bandyopadhyay, Amit ^{[1
]}

机构：

[1] Washington State Univ, Sch Mech & Mat Engn, WM Keck Biomed Mat Res Lab, Pullman, WA 99164 USA

[2] Jadavpur Univ, Dept Mech Engn, Kolkata 700032, India

来源：

MATERIALS SCIENCE & ENGINEERING C-BIOMIMETIC AND SUPRAMOLECULAR SYSTEMS | 2009年 / 29卷 / 04期

关键词：

Hydroxyapatite; Tri-calcium phosphate; Microwave sintering; Mechanical properties; HYDROXYAPATITE; BONE; ALUMINA; FIELD;

D O I：

10.1016/j.msec.2008.09.008

中图分类号：

T [工业技术];

学科分类号：

120111 [工业工程];

摘要：

Microwave sintering of hydroxyapatite (HAP) and tri-calcium phosphate (TCP) ceramics were studied using a commercial 2.45 GHz. 3 KW fully automated microwave system. Four different powder compositions, apart from pure HAP and TCP, were prepared with small amount of different oxide additives e.g., magnesium oxide, zinc oxide and titanium oxide. All samples were densified at 1250 degrees C for 30 min. Sintered samples had high density and homogeneous microstructure for all compositions. Phase analysis using XRD showed no major variations from starting materials. Presence of additives increased compressive strength between 100 and 200%. Fractured surfaces showed clear signs of intergranular fracture in undoped HAP and TCP while in doped samples, fracture modes were either transgranular or mixed mode. In comparison to conventional sintering. microwave sintering of calcium phosphate ceramics was found to be economically exciting due to substantial reduction in processing time and energy expenditure due to volumetric heating of samples. (C) 2008 Elsevier B.V. All rights reserved.

引用

页码：1144 / 1149

页数：6

共 21 条

[1]

Calcium phosphate-based resorbable ceramics:: Influence of MgO, ZnO, and SiO2 dopants [J].

Bandyopadhyay, Amit ;

Bernard, Sheldon ;

Xue, Weichang ;

Bose, Susmita .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2006, 89 (09) :2675-2688

[2]

Hydroxyapatite nanopowders: Synthesis, densification and cell-materials interaction [J].

Banerjee, Ashis ;

Bandyopadhyay, Amit ;

Bose, Susmita .

MATERIALS SCIENCE & ENGINEERING C-BIOMIMETIC AND SUPRAMOLECULAR SYSTEMS, 2007, 27 (04) :729-735

[3]

CAI J, 1996, J GRADUATE SCH ACAD, V138, P163

[4]

STRUCTURAL ARRANGEMENTS AT THE INTERFACE BETWEEN PLASMA-SPRAYED CALCIUM PHOSPHATES AND BONE [J].

DEBRUIJN, JD ;

BOVELL, YP ;

VANBLITTERSWIJK, CA .

BIOMATERIALS, 1994, 15 (07) :543-550

[5]

DEGROOT K, 1984, NOYES, P447

[6]

Bioactive ceramics: the effect of surface reactivity on bone formation and bone cell function [J].

Ducheyne, P ;

Qiu, Q .

BIOMATERIALS, 1999, 20 (23-24) :2287-2303

[7]

MICROWAVE SINTERING OF HYDROXYAPATITE CERAMICS [J].

FANG, Y ;

AGRAWAL, DK ;

ROY, DM ;

ROY, R .

JOURNAL OF MATERIALS RESEARCH, 1994, 9 (01) :180-187

[8]

MICROWAVE FIELD ENHANCEMENT OF CHARGE-TRANSPORT IN SODIUM-CHLORIDE [J].

FREEMAN, SA ;

BOOSKE, JH ;

COOPER, RF .

PHYSICAL REVIEW LETTERS, 1995, 74 (11) :2042-2045

[9]

Strength degradation of nonrandom porous ceramic structures under uniaxial compressive loading [J].

Hattiangadi, Ashwin, 2000, American Ceramic Soc, Westerville (83)

[10]

Effects of designed tubular porosity on compressive strengths of honeycomb ceramics [J].

Hattiangadi, A ;

Bandyopadhyay, A .

JOURNAL OF MATERIALS SCIENCE, 2004, 39 (14) :4575-4586

← 1 2 3 →