The effect of the microstructure on the magnetic interactions in CoFe-AgCu granular films: From demagnetizing to magnetizing interactions

The sign and strength of the dominant magnetic interactions in Co34Fe8Ag54Cu4 granular films were modified by changing the microstructure through annealing. Magnetic force micrographs showed that in the as-cast sample the magnetic moments of neighboring grains tended to be arranged parallel along a direction out of the film plane, forming elongated magnetic clusters that were themselves aligned antiparallel, with dominant demagnetizing interactions. This is a direct evidence that an uncompensated antiferromagneticlike microstructure is stabilized below the volume percolation threshold. However, in the sample annealed at 750 degrees C the particle growth led to large in-plane ferromagneticlike clusters with dominant magnetizing interactions. Thus, in this letter we present direct correlation of interactions effects with magnetic measurements and show that Delta M plots correlate with changes in the magnetic microstructure in these systems. (C) 1997 American Institute of Physics.