Mechanical activation of the synthesis reaction of BaTiO3 from a mixture of BaCO3 and TiO2 powders

被引:108
作者
Gomez-Yañez, C [1 ]
Benitez, C [1 ]
Balmori-Ramirez, H [1 ]
机构
[1] Inst Politecn Nacl, ESIQIE, Dept Met Engn, Mexico City 07738, DF, Mexico
关键词
powders; solid state reaction; BaTiO3;
D O I
10.1016/S0272-8842(99)00053-X
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The influence of long term milling in an attritor of a mixture of BaCO3 and TiO2 powders on the reaction synthesis of BaTiO3 was studied. Thermal analysis (TG and DTA) of the unmilled and milled powders and X-ray diffraction of powders calcined at different temperatures were undertaken. Milling does not change the reaction sequence between BaCO3 and TiO2. BaTiO3 and Ba2TiO3 are produced in both kinds of powders. However, milling reduces the formation temperature and accelerates the formation rate of these two phases. The production of final BaTiO3 is incomplete in the milled powder, probably because of the formation of big crystals of Ba2TiO4. As a consequence, the milled powder contains large amounts of Ba2TiO4 after calcination at 1200 degrees C. Milling produces allotropic transformations in TiO2 from anatase phase, to alpha-PbO2-like phase and finally to rutile structure. (C) 2000 Elsevier Science Ltd and Techna S.r.l. All rights reserved.
引用
收藏
页码:271 / 277
页数:7
相关论文
共 14 条
[1]  
Abe O, 1996, MATER SCI FORUM, V225, P563
[2]   BARIUM-TITANATE NOBLE-METAL LAMINATES PREPARED BY THE OXIDATION OF SOLID METALLIC PRECURSORS [J].
ANTONY, MM ;
SANDHAGE, KH .
JOURNAL OF MATERIALS RESEARCH, 1993, 8 (11) :2968-2977
[3]   SYNTHESIS REACTION OF METATITANATE BATIO3 .1. EFFECT OF THE GASEOUS ATMOSPHERE UPON THE THERMAL EVOLUTION OF THE SYSTEM BACO3-TIO2 [J].
BEAUGER, A ;
MUTIN, JC ;
NIEPCE, JC .
JOURNAL OF MATERIALS SCIENCE, 1983, 18 (10) :3041-3046
[4]   SYNTHESIS REACTION OF METATITANATE BATIO3 .2. STUDY OF SOLID SOLID REACTION INTERFACES [J].
BEAUGER, A ;
MUTIN, JC ;
NIEPCE, JC .
JOURNAL OF MATERIALS SCIENCE, 1983, 18 (12) :3543-3550
[5]   INFLUENCE OF THE NATURE OF MILLING MEDIA ON PHASE-TRANSFORMATIONS INDUCED BY GRINDING IN SOME OXIDES [J].
BEGINCOLIN, S ;
LECAER, G ;
ZANDONA, M ;
BOUZY, E ;
MALAMAN, B .
JOURNAL OF ALLOYS AND COMPOUNDS, 1995, 227 (02) :157-166
[6]  
Boldyrev V V., 1990, Russ. Chem. Rev, V14, P105
[7]   COPPER-ALLOYS AND COBALT-ALLOYS MADE BY MECHANICAL ALLOYING [J].
CABANASMORENO, JG ;
LOPEZHIRATA, VM .
MATERIALS TRANSACTIONS JIM, 1995, 36 (02) :218-227
[8]   OBSERVATION OF A HIGH-PRESSURE POLYMORPH OF TITANIA BY VIBRATIONAL BALL-MILLING [J].
CHAUDHURI, J ;
RAM, ML ;
SARKAR, BK .
JOURNAL OF MATERIALS SCIENCE, 1994, 29 (13) :3484-3488
[9]  
DELATORRE S, 1995, THESIS KYOTO U JAPAN
[10]  
HERBERT JM, 1985, CERAMIC DIELECTRIC C