Microstructural evolution in T24, a modified 2(1/4)Cr-1Mo steel during creep after different heat treatments

被引:19
作者
Aghajani, A. [1 ]
Somsen, Ch. [1 ]
Pesicka, J. [2 ]
Bendick, W. [3 ]
Hahn, B. [4 ]
Eggeler, G. [1 ]
机构
[1] Ruhr Univ Bochum, Inst Werkstoffe, D-44801 Bochum, Germany
[2] Charles Univ Prague, Fac Math & Phys, Dept Met Phys, CR-12116 Prague, Czech Republic
[3] Salzgitter Mannesmann Forsch GmbH, D-47251 Duisburg, Germany
[4] Vallourec & Mannesmann Tubes, D-40472 Dusseldorf, Germany
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2009年 / 510-11卷
关键词
Creep of bainitic steels; Cr-Mo steels; Heat treatment; Microstructure; Carbides; Transmission electron microscopy; 2.25CR-1MO STEEL; CARBIDE REACTIONS; PHASE-EQUILIBRIA; 773-993; K; MO; PRECIPITATION; STRENGTH;
D O I
10.1016/j.msea.2008.08.049
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
A crept modified 2(1/4)Cr-Mo steel (T24) was investigated in order to understand differences in creep behavior which are related to different cooling rates after austenitizing (air-cooling and water quenching). Two 823 K creep stress levels were compared, 150 MPa (rupture times of the order of: 50,000 h) and 200 MPa (rupture times of the order of: 500 h). The air cooled specimens showed lower rupture times at 200 MPa (short term creep conditions) while the differences in rupture times were not pronounced at 150 MPa (long term creep tests). The minimum creep rates were always faster for the air cooled material state. Microscopic techniques, documenting length scales from the mm (optical microscopy) to the nm range (transmission electron microscopy) were used to study microstructures. Water quenching results in the formation of martensite while air cooling produces bainitic microstructures. After creep, the water cooled specimens still show a finer microstructure (tempered martensite which is equivalent to a fine bainitic structure) than the air cooled specimens (coarse bainite). This mesoscopic microstructural difference can be documented using optical microscopy and scanning electron microscopy, and accounts for the differences in minimum creep rates and rupture times. No significant differences were found when using transmission electron microscopy (TEM) to study the two microstructures (fine and coarse bainite) after creep. M23C6 (on internal interfaces), MX precipitates (on internal interfaces and in the matrix) and M6C carbides were detected in both microstructures. TEM observations suggest that interactions between small and stable MX precipitates and dislocations provide the high creep strength. Long term creep conditions result in the formation of molybdenum-rich M6C carbides which were not observed after short term creep exposure. These M6C carbides form close to M23C6 particles. Moreover, it was found that the Mo-content of the MX precipitates increases during long term creep. Crown Copyright (C) 2008 Published by Elsevier B.V. All rights reserved.
引用
收藏
页码:130 / 135
页数:6
相关论文
共 23 条
[1]   Evolution of microstructure and deformation resistance in creep of tempered martensitic 9-12%Cr-2%W-5%Co steels [J].
Agamennone, R. ;
Blum, W. ;
Gupta, C. ;
Chakravartty, J. K. .
ACTA MATERIALIA, 2006, 54 (11) :3003-3014
[2]   THERMO-CALC & DICTRA, computational tools for materials science [J].
Andersson, JO ;
Helander, T ;
Höglund, LH ;
Shi, PF ;
Sundman, B .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2002, 26 (02) :273-312
[3]  
ANDREWS KW, 1972, J IRON STEEL I, V210, P337
[4]  
Baker RG., 1959, Journal of Iron and Steel Institute, V192, P257
[5]   New low alloy heat resistant ferritic steels T/P23 and T/P24 for power plant application [J].
Bendick, W. ;
Gabrel, J. ;
Hahn, B. ;
Vandenberghe, B. .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2007, 84 (1-2) :13-20
[6]  
De AK, 2003, ADV MATER PROCESS, V161, P27
[7]   THE EFFECT OF LONG-TERM CREEP ON PARTICLE COARSENING IN TEMPERED MARTENSITE FERRITIC STEELS [J].
EGGELER, G .
ACTA METALLURGICA, 1989, 37 (12) :3225-3234
[8]   Precipitation in 9Cr-1Mo steel after creep deformation [J].
Furtado, H. C. ;
de Almeida, L. H. ;
Le May, I. .
MATERIALS CHARACTERIZATION, 2007, 58 (01) :72-77
[9]   Identification of the precipitates by TEM and EDS in X20CrMoV12.1 after long-term service at elevated temperature [J].
Hu Zheng-Fei ;
Yang Zhen-Guo .
Journal of Materials Engineering and Performance, 2003, 12 (1) :106-111
[10]   MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF A 3CR-1.5MO STEEL [J].
KLUEH, RL ;
NASRELDIN, AM .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (07) :1279-1290