Application of polyaniline/nylon composites coating for corrosion protection of steel

In this research, we investigated the corrosion inhibition properties of polished steel plates (low carbon) coated with a polyaniline (emeraldine base form) blend with nylon 66 (termed PANi/Ny) via cast method with formic acid as the solvent. Polyaniline (PANi) was prepared chemically from aqueous solution using aniline (0.2 M) as a monomer and ammonium persulfate (0.2 M) as an oxidant. The polymer powder produced was changed into emeraldine base (EB) form after treatment with dilute ammonia solution (0.5 M) in order to do further processing. The corrosion experiments were performed in the open circuit, exposing samples to different aggressive and corrosive conditions (e.g., NaCl, HCl). To produce a good comparison, the corrosion study was performed on both polymer-coated and bare-steel samples. Corrosion monitoring was performed by simple immersion tests and determination of the concentration of iron ions and metal weight loss in test solutions. It was found that PANi/Ny coatings can provide an anodic protection against corrosive environments in which the metals are exposed. The corrosion rate for the polymer coated steel was significantly lower than the bare steel (similar to 10-15 times).