Free volume and glass transition in ethylene/1-octene copolymers:: positron lifetime studies and dynamic mechanical analysis

被引:46
作者
Kilburn, D
Bamford, D
Lüpke, T
Dlubek, G
Menke, TJ
Alam, MA
机构
[1] ITA Inst Innovat Technol GmbH, D-06120 Halle An Der Saale, Germany
[2] Univ Bristol, HH Wills Phys Lab, Bristol BS8 1TL, Avon, England
[3] Univ Halle Wittenberg, Fachbereich Ingenieurwissensch, D-06099 Halle An Der Saale, Germany
基金
英国工程与自然科学研究理事会;
关键词
ethylene-octene copolymers; glass transition; free volume;
D O I
10.1016/S0032-3861(02)00663-8
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Semicrystalline ethylene/1-octene copolymers (P(E-co-O)) with a content of 1-octene comonomer, w(O), between 7 and 24 wt% and a crystallinity X-c between 50 and 10% and a high-density polyethylene (HDPE, X-c = 70%) were studied in the temperature range between 115 K and (300-350) K by positron annihilation lifetime spectroscopy (PALS) and dynamic mechanical analysis (DMA). The samples were characterised by differential scanning calorimetry (DSC) and wide-angle X-ray scattering (WAXS). The T(g)s estimated from the thermal expansion of the local free volume estimated from the PALS data decrease linearly with w(O) between 251 K (extrapolated to w(O) = 0) and 220 K (w(O) = 24 wt%). They agree very well with those estimated from DMA (loss modulus E") and DSC. However, the T(g)s obtained from the maximum of tan 8 do not agree with all of the others, inparticular for higher crystallinities. For HDPE, any indication of glass transition could not be observed. From this it was concluded that the whole amorphous phase in this highly crystalline polymer is immobile. From the variation of the thermal expansivity of the local free volume the fractions of the mobile and immobile amorphous phase are estimated. It was observed that the o-Ps intensity shows a minimum at T-min approximate to T-g + 10 K. (C) 2002 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码:6973 / 6983
页数:11
相关论文
共 92 条
[1]  
ALSLEBEN M, 2000, THERMOCHIM ACTA, V238, P294
[2]   Melting and crystallization of poly(ethylene-co-octene) measured by modulated dsc and temperature-resolved X-ray diffraction [J].
Androsch, R .
POLYMER, 1999, 40 (10) :2805-2812
[3]   The local free volume, glass transition, and ionic conductivity in a polymer electrolyte: A positron lifetime study [J].
Bamford, D ;
Dlubek, G ;
Reiche, A ;
Alam, MA ;
Meyer, W ;
Galvosas, P ;
Rittig, F .
JOURNAL OF CHEMICAL PHYSICS, 2001, 115 (15) :7260-7270
[4]  
Ban M, 1996, J POLYM SCI POL PHYS, V34, P1189, DOI 10.1002/(SICI)1099-0488(199605)34:7<1189::AID-POLB2>3.0.CO
[5]  
2-R
[6]   Direct computation of the free volume fraction in amorphous polymers from positron lifetime measurements [J].
Bandzuch, P ;
Kristiak, J ;
Sausa, O ;
Zrubcová, J .
PHYSICAL REVIEW B, 2000, 61 (13) :8784-8792
[7]  
Bartos J, 2000, MACROMOL SYMP, V158, P111, DOI 10.1002/1521-3900(200008)158:1<111::AID-MASY111>3.0.CO
[8]  
2-N
[9]   Free volume and microscopic dynamics in amorphous polymers [J].
Bartos, J ;
Kristiak, J ;
Kanaya, T .
PHYSICA B, 1997, 234 :435-436
[10]   Free-volume microstructure of glycerol and its supercooled liquid-state dynamics [J].
Bartos, J ;
Sausa, O ;
Kristiak, J ;
Blochowicz, T ;
Rössler, E .
JOURNAL OF PHYSICS-CONDENSED MATTER, 2001, 13 (50) :11473-11484