Organometallic synthesis and magnetic properties of ferromagnetic Sm-Co nanoclusters

被引:45
作者
Ono, K [1 ]
Kakefuda, Y [1 ]
Okuda, R [1 ]
Ishii, Y [1 ]
Kamimura, S [1 ]
Kitamura, A [1 ]
Oshima, M [1 ]
机构
[1] Univ Tokyo, Sch Engn, Bunkyo Ku, Tokyo 1138656, Japan
关键词
D O I
10.1063/1.1456407
中图分类号
O59 [应用物理学];
学科分类号
摘要
We have successfully prepared Sm-Co composite nanoclusters using liquid-phase organometallic synthesis. The chemical composition was determined by quantitative x-ray fluorescence analysis and it is found that the composition of synthesized Sm-Co nanoclusters was Sm poor while the Sm-Co nanoclusters with required composition could be obtained in starting from the excess Sm(acac)(3). From the transmission electron microscopy measurements, the Sm-Co nanoclusters have the uniform size with the diameter of 9 nm. The crystalline structure was fcc which is different from that of bulk SmCo alloy with the same Sm and Co content. The magnetic property was observed by superconducting quantum interference magnetometer and shows the ferromagnetic characteristics. (C) 2002 American Institute of Physics.
引用
收藏
页码:8480 / 8482
页数:3
相关论文
共 9 条
[1]  
Alvistos A. P., 1996, SCIENCE, V271, P933
[2]   ''Coulomb staircase'' at room temperature in a self-assembled molecular nanostructure [J].
Andres, RP ;
Bein, T ;
Dorogi, M ;
Feng, S ;
Henderson, JI ;
Kubiak, CP ;
Mahoney, W ;
Osifchin, RG ;
Reifenberger, R .
SCIENCE, 1996, 272 (5266) :1323-1325
[3]   Minimum field strength in precessional magnetization reversal [J].
Back, CH ;
Allenspach, R ;
Weber, W ;
Parkin, SSP ;
Weller, D ;
Garwin, EL ;
Siegmann, HC .
SCIENCE, 1999, 285 (5429) :864-867
[4]   Spin-dependent tunneling in self-assembled cobalt-nanocrystal superlattices [J].
Black, CT ;
Murray, CB ;
Sandstrom, RL ;
Sun, SH .
SCIENCE, 2000, 290 (5494) :1131-1134
[5]   Reversible tuning of silver quantum dot monolayers through the metal-insulator transition [J].
Collier, CP ;
Saykally, RJ ;
Shiang, JJ ;
Henrichs, SE ;
Heath, JR .
SCIENCE, 1997, 277 (5334) :1978-1981
[6]   Magnetization directions of individual nanoparticles [J].
Majetich, SA ;
Jin, Y .
SCIENCE, 1999, 284 (5413) :470-473
[7]   SELF-ORGANIZATION OF CDSE NANOCRYSTALLITES INTO 3-DIMENSIONAL QUANTUM-DOT SUPERLATTICES [J].
MURRAY, CB ;
KAGAN, CR ;
BAWENDI, MG .
SCIENCE, 1995, 270 (5240) :1335-1338
[8]   Colloidal nanocrystal shape and size control: The case of cobalt [J].
Puntes, VF ;
Krishnan, KM ;
Alivisatos, AP .
SCIENCE, 2001, 291 (5511) :2115-2117
[9]   Monodisperse FePt nanoparticles and ferromagnetic FePt nanocrystal superlattices [J].
Sun, SH ;
Murray, CB ;
Weller, D ;
Folks, L ;
Moser, A .
SCIENCE, 2000, 287 (5460) :1989-1992