Fractionation of benzene/n-hexane mixtures by pervaporation using polyurethane membranes

In the present work polyurethane membranes obtained from different polyester/MDI-based polymers were used to separate benzene/n-hexane mixtures by pervaporation. In pervaporation experiments, with a 50% wt feed at room temperature, permeate fluxes in the range of 0.3 to 3.2 Kg/m(2)h (10 mu m membrane thickness) and selectivity in the range of 3.8 to 5.6 were obtained. The permeate was always enriched in benzene. Taking into account the compromise between flux and selectivity, the best performance membrane was selected for complementary sorption and pervaporation experiments. Results show that selectivity increases and the permeation flux decreases when the benzene concentration in the feed decreases. In the present application, results also show that sorption is the main factor for selectivity. Using the distillation azeotropic mixture as feed, almost no influence of temperature on selectivity was observed in the range of 25 degrees C to 56 degrees C. The permeate flux increases seven-fold, while selectivity remains constant near 8.0.