Thin hard coatings fracture propagation during the impact test

One of the most significant applications of the impact test is to investigate thin hard coatings fatigue properties. Herein the test conditions and duration up to the film damage initiation, are considered in order to determine the critical stresses associated with the coating fatigue strength. Moreover, the subsequent film damage propagation is a significant mechanism as well, since it refers to the ability of the coating to withstand loads after its fatigue damage initiation. In order to describe the film fracture propagation the failed area ratio was introduced and an algorithm to determine this magnitude developed, based on the analysis of imprint scanning electron microscopy graphs. The application of the coating failed area ratio will be demonstrated in various impact test film cases, also with superficial thin layers. The top layers do not affect, in general, the failure initiation of the basic coating. However, according to the obtained results, the superficial films influence the basic coating failure propagation rate during the impact test. (C) 2004 Elsevier B.V. All rights reserved.