Development and performance of thin steel reinforced MgB2 wires and low-temperature in situ processing for further improvements

被引：27

作者：

Goldacker, W ^{[1
]}

Schlachter, SI ^{[1
]}

Obst, B ^{[1
]}

Liu, B ^{[1
]}

Reiner, J ^{[1
]}

Zimmer, S ^{[1
]}

机构：

[1] Forschungszentrum Karlsruhe, Inst Tech Phys, D-76021 Karlsruhe, Germany

来源：

SUPERCONDUCTOR SCIENCE & TECHNOLOGY | 2004年 / 17卷 / 05期

关键词：

D O I：

10.1088/0953-2048/17/5/055

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

In mono- and multifilamentary MgB2 wires with small filament diameters a homogeneous and fine-grained MgB2 phase is required for high transport currents and reactions with the sheath have to be avoided. Taking this into account we developed very thin steel reinforced MgB2 wires for application as current leads in a research satellite. In situ phase formation in the wire from Mg + B powders was chosen as the most favourable method to achieve good grain connectivity and thus high transport currents. We tested the current lead wires with transport current measurements and investigated the mechanical performance with applied tensile and bending strains. With an improved processing route applying a low-temperature anneal the superconducting properties of standard undoped in situ MgB2 wires could be further improved and critical current densities of 38 kA cm(-2) at 6 T and 10 kA cm(-2) at 8 T, 4.2 K could be achieved.

引用

页码：S363 / S368

页数：6

共 21 条

[1] Continuous- and batch-processed MgB2/Fe strands -: transport and magnetic properties [J].

Collings, EW ;

Lee, E ;

Sumption, MD ;

Tomsic, M ;

Wang, XL ;

Soltanian, S ;

Dou, SX .

PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 386 :555-559

[2] Transport critical current density in Fe-sheathed nano-SiC doped MgB2 wires [J].

Dou, SX ;

Horvat, J ;

Soltanian, S ;

Wang, XL ;

Qin, MJ ;

Zhou, SH ;

Liu, HK ;

Munroe, PG .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2003, 13 (02) :3199-3202

[3] High performance new MgB2 superconducting hollow wires [J].

Giunchi, G ;

Ceresara, S ;

Ripamonti, G ;

Di Zenobio, A ;

Rossi, S ;

Chiarelli, S ;

Spadoni, M ;

Wesche, R ;

Bruzzone, PL .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2003, 16 (02) :285-291

[4] Composite Cu/Fe/MgB2 superconducting wires and MgB2/YSZ/Hastelloy coated conductors for ac and dc applications [J].

Glowacki, BA ;

Majoros, M ;

Vickers, M ;

Eisterer, M ;

Toenies, S ;

Weber, HW ;

Fukutomi, M ;

Komori, K ;

Togano, K .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2003, 16 (02) :297-305

[5] Mechanical properties of reinforced MgB2 wires [J].

Goldacker, MW ;

Schlachter, SI ;

Reiner, J ;

Zimmer, S ;

Nyilas, A ;

Kiesel, H .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2003, 13 (02) :3261-3264

[6] Considerations on critical currents and stability of MgB2 wires made by different preparation routes [J].

Goldacker, W ;

Schlachter, SI ;

Liu, B ;

Obst, B ;

Klimenko, E .

PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2004, 401 (1-4) :80-86

[7]

Goldacker W, 2002, AIP CONF PROC, V614, P469, DOI 10.1063/1.1472575

[8] Influence of mechanical reinforcement of MgB2 wires on the superconducting properties [J].

Goldacker, W ;

Schlachter, SI .

PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2002, 378 (PART 2) :889-893

[9] High transport currents in mechanically reinforced MgB2 wires [J].

Goldacker, W ;

Schlachter, SI ;

Zimmer, S ;

Reiner, H .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2001, 14 (09) :787-793

[10]

GOLDACKER W, 2004, UNPUB SUPERCOND SCI

← 1 2 3 →