Electrical and electro-chemical characterisation of La0.99Fe1-xNixO3-δ perovskites

被引：19

作者：

Kammer, K. ^{[1
]}

Mikkelsen, L. ^{[1
]}

Bilde-Sorensen, J. B. ^{[1
]}

机构：

[1] Riso Natl Lab, Dept Fuel Cells & Solid State Chem, DK-4000 Roskilde, Denmark

来源：

JOURNAL OF SOLID STATE ELECTROCHEMISTRY | 2006年 / 10卷 / 11期

关键词：

D O I：

10.1007/s10008-006-0153-8

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

La0.99Fe1-xNixO3-delta (LFN, 0 < x < 0.6) perovskites were synthesised by a solid-state route and were characterised by powder XRD, dilatometry, four-point DC conductivity measurements and electro-chemical impedance spectroscopy (EIS) on cone-shaped electrodes using a Ce1.9Gd0.1O1.95 (CGO10) electrolyte. All the compounds were of single phase, and they belong to either the cubic or the hexagonal crystal system. The thermal expansion coefficient (TEC) was in the range 10.7* 10(-6) K-1 to 13.4* 10(-6) K-1, which continued to increase with increasing nickel content. The highest electronic conductivity was measured for the composition La0.99Fe0.4Ni0.6O3-delta, giving a value of 670 S/cm at 380 degrees C. The highest electrochemical performance was measured for the composition La0.99Fe0.4Ni0.6O3-delta giving an area specific resistance as low as 5.5 Omega cm(2) at 600 degrees C based on EIS measurements on a cone-shaped electrode. Composite cathodes made from La0.99Fe0.4Ni0.6O3-delta and CGO10 revealed a rather low performance due to an un-optimised micro-structure.

引用

页码：934 / 940

页数：7

共 29 条

[1] LaNi0.6Fe0.4O3 as a cathode contact material for solid oxide fuel cells [J].

Basu, RN ;

Tietz, F ;

Teller, O ;

Wessel, E ;

Buchkremer, HP ;

Stöver, D .

JOURNAL OF SOLID STATE ELECTROCHEMISTRY, 2003, 7 (07) :416-420

[2] Structural study of LaNixFe1-xO3 prepared from precursor salts [J].

Bontempi, E ;

Garzella, C ;

Valetti, S ;

Depero, LE .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2003, 23 (12) :2135-2142

[3]

BOUKAMP BA, 1996, EQUICVRT

[4] Defect chemical modeling of (La,Sr)(Co,Fe)O3-δ [J].

Bucher, E ;

Sitte, W .

JOURNAL OF ELECTROCERAMICS, 2004, 13 (1-3) :779-784

[5] An investigation of LaNi1-xFexO3 as a cathode material for solid oxide fuel cells [J].

Chiba, R ;

Yoshimura, F ;

Sakurai, Y .

SOLID STATE IONICS, 1999, 124 (3-4) :281-288

[6]

Chiba R, 1999, ELEC SOC S, V99, P453

[7] GLYCINE NITRATE COMBUSTION SYNTHESIS OF OXIDE CERAMIC POWDERS [J].

CHICK, LA ;

PEDERSON, LR ;

MAUPIN, GD ;

BATES, JL ;

THOMAS, LE ;

EXARHOS, GJ .

MATERIALS LETTERS, 1990, 10 (1-2) :6-12

[8]

*COMS, 2005, FEMLAB 3 1

[9] Crystal structure refinement and stability of LaFexNi1-xO3 solid solutions [J].

Falcon, H ;

Goeta, AE ;

Punte, G ;

Carbonio, RE .

JOURNAL OF SOLID STATE CHEMISTRY, 1997, 133 (02) :379-385

[10] STUDY OF THE HETEROGENEOUS DECOMPOSITION OF HYDROGEN-PEROXIDE - ITS APPLICATION TO THE DEVELOPMENT OF CATALYSTS FOR CARBON-BASED OXYGEN CATHODES [J].

FALCON, H ;

CARBONIO, RE .

JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1992, 339 (1-2) :69-83

← 1 2 3 →