Properties of Co-Mo coatings obtained by electrodeposition at pH 6.6

被引:51
作者
Gómez, E
Pellicer, E
Alcobé, X
Vallés, E
机构
[1] Univ Barcelona, Dept Quim Fis, E-08028 Barcelona, Spain
[2] Univ Barcelona, Serv Cientificiotecn, E-08028 Barcelona, Spain
关键词
cobalt-molybdenum alloy; electrodeposition; magnetic films; X-ray diffraction;
D O I
10.1007/s10008-004-0495-z
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
Cobalt-molybdenum coatings were prepared by electrodeposition in a sulfate-citrate bath and their morphology, structure and magnetic properties were analysed. Concentrations of 0.1 mol dm(-3) CoSO4 and 0.005 mol dm(-3) Na2MoO4 at pH 6.6 led to Co-Mo deposits of 20-23% Mo that can be grown to several microns over graphite or copper substrates. At low deposition potentials or current densities, the deposits presented a close-packed hexagonal structure (hcp) that evolved to a (100)+(110) preferred orientation and acicular morphology as the deposit thickness increased. When the deposition potential or the current density was made more negative, a mixed crystalline+amorphous structure was obtained. The degree of crystallinity depended on the thickness: thin films were more amorphous than the thicker ones. Co-Mo deposits showed lower saturation magnetization (M-s) and coercivity (H-c) than the pure cobalt deposits. The crystalline+amorphous films showed the lowest H-c values (around 40 Oe).
引用
收藏
页码:497 / 504
页数:8
相关论文
共 21 条
[1]   KINETIC CORRELATIONS IN CODEPOSITION OF COATINGS OF MOLYBDENUM IRON GROUP METAL-ALLOYS [J].
BELTOWSKALEHMAN, E .
JOURNAL OF APPLIED ELECTROCHEMISTRY, 1990, 20 (01) :132-138
[2]  
Brenner A., 1963, ELECTRODEPOSITION AL, V1
[3]  
CHASSAING E, 1995, J APPL ELECTROCHEM, V25, P667, DOI 10.1007/BF00241928
[4]   MECHANISM OF NICKEL MOLYBDENUM ALLOY ELECTRODEPOSITION IN CITRATE ELECTROLYTES [J].
CHASSAING, E ;
QUANG, KV ;
WIART, R .
JOURNAL OF APPLIED ELECTROCHEMISTRY, 1989, 19 (06) :839-843
[5]   INFLUENCE OF SUBSTRATE ON THE ELECTRODEPOSITION OF NICKEL-MOLYBDENUM ALLOYS [J].
CROUSIER, J ;
EYRAUD, M ;
CROUSIER, JP ;
ROMAN, JM .
JOURNAL OF APPLIED ELECTROCHEMISTRY, 1992, 22 (08) :749-755
[6]  
Friend WZ, 1980, CORROSION NICKEL NIC, P95
[7]   Influence of the bath composition and the pH on the induced cobalt-molybdenum electrodeposition [J].
Gómez, E ;
Pellicer, E ;
Vallés, E .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2003, 556 :137-145
[8]   Electrodeposited cobalt-molybdenum magnetic materials [J].
Gómez, E ;
Pellicer, E ;
Vallés, E .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2001, 517 (1-2) :109-116
[9]   Hydrogen evolving activity on nickel-molybdenum deposits using experimental strategies [J].
Hu, CC ;
Weng, CY .
JOURNAL OF APPLIED ELECTROCHEMISTRY, 2000, 30 (04) :499-506
[10]  
Klavunde K. J., 2001, NANOSCALE MAT CHEM