Poly (ether ether ketone) derivatives: Synthetic route and characterization of nitrated and sulfonated polymers

Nitrated and sulfonated poly (ether ether ketone) [SNPEEK] samples were prepared through sulfonation of nitrated PEEK (NPEEK) at different temperatures resulting in polymers with distinct sulfonation degrees (SD). The sulfonation occurred preferentially in the hydroquinone segment even after 81% of this moiety had been nitrated. Sulfonation in the benzophenone moiety was achieved only in 16% of this segment at the reaction temperature of 80 degrees C. The substitution degree was obtained through the TG curves, and values were in agreement with H-1 NMR data when SD is much higher as ND (nitration degree). The highest SD obtained was 72%. Membranes Of the sulfonated and nitrated PEEK (SNPEEK) were prepared by casting and showed good ductility depending on the substitution degree, with proton conductivity in the order of 10(-2) S cm(-1), all important characteristic in some applications. such as in fuel cells. (C) 2008 Elsevier B.V. All rights reserved.