Corrosion experiments in flowing LBE at 450°C

被引：16
作者：
Benamati, G.
Gessi, A. [1 ]
Zhang, Ping-Zhu
机构：
[1] ENEA CR Brasimone, I-40032 Camugnano, BO, Italy
[2] CIAE, Beijing, Peoples R China
来源：
JOURNAL OF NUCLEAR MATERIALS | 2006年 / 356卷 / 1-3期
关键词：
D O I：
10.1016/j.jnucmat.2006.05.035
中图分类号：
T [工业技术];
学科分类号：
08 [工学];
摘要：
The corrosion behaviour of AISI 316L steel is being investigated in flowing lead-bismuth eutectic (LBE) at 450 degrees C. The tests are performed in the LECOR (lead corrosion) loop, at low oxygen activity in LBE. The preliminary results presented in this paper refer to AISI 316L stainless steel and show the start of a corrosion mechanism with a small transfer of Cr from the inner part of the steel matrix to the outer one. This paper reports only preliminary results, obtained after 1000 h of test. (c) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码：198 / 202
页数：5
相关论文
共 7 条
[1]
Corrosion behaviour of stainless steels in flowing LBE at low and high oxygen concentration [J].
Aiello, A ;
Azzati, M ;
Benamati, G ;
Gessi, A ;
Long, B ;
Scaddozzo, G .
JOURNAL OF NUCLEAR MATERIALS, 2004, 335 (02) :169-173
[2]
AZZATI M, 2003, HSAR014 ENEA
[3]
SINGLE-CRYSTAL RAMAN SPECTRA OF NEARLY OPAQUE MATERIALS - IRON(III) OXIDE AND CHROMIUM(III) OXIDE [J].
BEATTIE, IR ;
GILSON, TR .
JOURNAL OF THE CHEMICAL SOCIETY A -INORGANIC PHYSICAL THEORETICAL, 1970, (06) :980-&
[4]
Corrosion behaviour of steels and refractory metals and tensile features of steels exposed to flowing PbBi in the LECOR loop [J].
Fazio, C ;
Ricapito, I ;
Scaddozzo, G ;
Benamati, G .
JOURNAL OF NUCLEAR MATERIALS, 2003, 318 :325-332
[5]
Compatibility tests on steels in molten lead and lead-bismuth [J].
Fazio, C ;
Benamati, G ;
Martini, C ;
Palombarini, G .
JOURNAL OF NUCLEAR MATERIALS, 2001, 296 :243-248
[6]
GESSI A, 2005, J MATER SCI, V40, P1
[7]
Results of steel corrosion tests in flowing liquid Pb/Bi at 420-600 °C after 2000 h [J].
Müller, G ;
Heinzel, A ;
Konys, J ;
Schumacher, G ;
Weisenburger, A ;
Zimmermann, F ;
Engelko, V ;
Rusanov, A ;
Markov, V .
JOURNAL OF NUCLEAR MATERIALS, 2002, 301 (01) :40-46
1