Soft magnetic bulk glassy Fe-B-Si-Nb alloys with high saturation magnetization above 1.5 T

被引:161
作者
Inoue, A [1 ]
Shen, B [1 ]
机构
[1] Tohoku Univ, Inst Mat Res, Sendai, Miyagi 9808577, Japan
关键词
iron-based alloy; bulk glassy alloy; copper mould casting; soft magnetic property; high saturation magnetization;
D O I
10.2320/matertrans.43.766
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
New Fe-based bulk glassy alloys were synthesized in the (Fe0.75B0.15Si0.10)((x)-x) Nb-x system by copper mould casting, The maximum diameter of the bulk glassy alloy rod was 0.5 mm at at% Nb, 1.0 mm at 2 at% Nb and 1.5 mm at 4 at% Nb. No glass transition is observed at 0 at% Nb, but the addition of Nb causes the appearance of glass transition before crystallization. The glass transition temperature (T-g) and crystallization temperature (T-g) of the bulk glassy rods were 815 K and 858 K, respectively for the 1 at% Nb alloy, and 835 K and 885 K. respectively, for the 4 at% Nb alloy. The reduced glass transition temperature (T-g/T-i) defined by the ratio of T-g to the liquidus temperature (T-I) was measured as 0.56 at 1 at%Nb, 0.57 at 2 at% Nb and 0.61 at 4 at% Nb. There is a tendency for T-g, DeltaT(k) (= T-x - T-g) and T-g/T-i to increase with increasing Nb content. The effect of Nb addition can be interpreted in the framework of the three component rule for the formation of bulk glassy alloys and the stabilization of supercooled liquid. The Fe-B-Si alloy satisfies the three component rules by the addition of Nb, The bulk glassy alloy rods exhibited good soft magnetic properties. i.e.. high saturation magnetization (I-s) of 1.47 to 1.51, low coercive force (H-c) of 2.9 to 3.7 A/m and Curie temperature of 593 to 684 K. The high I-s and low H-c, as well a the formation of bulk glassy allots in the simple alloy system are promising as a new type of soft magnetic bulk alloy.
引用
收藏
页码:766 / 769
页数:4
相关论文
共 24 条
[1]  
HAGIWARA M, 1981, SCI REP RES TOHOKU A, V29, P351
[2]   Effect of additional elements (M) on the thermal stability of supercooled liquid in Fe(72-x)Al(5)Ga(2)P(11)C(6)B(4)M(x) glassy alloys [J].
Inoue, A ;
Gook, JS .
MATERIALS TRANSACTIONS JIM, 1996, 37 (01) :32-38
[3]   New bulk amorphous Fe-(Co,Ni)-M-B (M=Zr,Hf,Nb,Ta,Mo,W) alloys with good soft magnetic properties [J].
Inoue, A ;
Zhang, T ;
Koshiba, H ;
Makino, A .
JOURNAL OF APPLIED PHYSICS, 1998, 83 (11) :6326-6328
[4]   Stabilization of metallic supercooled liquid and bulk amorphous alloys [J].
Inoue, A .
ACTA MATERIALIA, 2000, 48 (01) :279-306
[5]   NEW AMORPHOUS MG-CE-NI ALLOYS WITH HIGH-STRENGTH AND GOOD DUCTILITY [J].
INOUE, A ;
OHTERA, K ;
KITA, K ;
MASUMOTO, T .
JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1988, 27 (12) :L2248-L2251
[6]   AL-LA-NI AMORPHOUS-ALLOYS WITH A WIDE SUPERCOOLED LIQUID REGION [J].
INOUE, A ;
ZHANG, T ;
MASUMOTO, T .
MATERIALS TRANSACTIONS JIM, 1989, 30 (12) :965-972
[7]   FE-BASED FERROMAGNETIC GLASSY ALLOYS WITH WIDE SUPERCOOLED LIQUID REGION [J].
INOUE, A ;
GOOK, JS .
MATERIALS TRANSACTIONS JIM, 1995, 36 (09) :1180-1183
[8]   Preparation and thermal stability of bulk amorphous Pd40Cu30Ni10P20 alloy cylinder of 72 mm in diameter [J].
Inoue, A ;
Nishiyama, N ;
Kimura, H .
MATERIALS TRANSACTIONS JIM, 1997, 38 (02) :179-183
[9]   Bulk amorphous alloys with high mechanical strength and good soft magnetic properties in Fe-TM-B (TM=IV-VIII group transition metal) system [J].
Inoue, A ;
Zhang, T ;
Takeuchi, A .
APPLIED PHYSICS LETTERS, 1997, 71 (04) :464-466
[10]   HIGH-STRENGTH BULK AMORPHOUS-ALLOYS WITH LOW CRITICAL COOLING RATES [J].
INOUE, A .
MATERIALS TRANSACTIONS JIM, 1995, 36 (07) :866-875