Microstructures of two-phase Ti-Cr alloys containing the TiCr2 Laves phase intermetallic

被引:41
作者
Chen, KC
Allen, SM
Livingston, JD
机构
[1] Dept. of Mat. Sci. and Engineering, Massachusetts Inst. of Technology, Cambridge
基金
美国能源部;
关键词
D O I
10.1557/JMR.1997.0203
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Microstructures of two-phase Ti-Cr alloys (Ti-rich bcc + TiCr2 and Cr-rich bcc + TiCr2) are analyzed. A variety of TiCr2 precipitate morphologies is encountered with different nominal alloy compositions and annealing temperatures. Lattice constants and crystal structures are determined by x-ray diffraction (XRD) and transmission electron microscopy (TEM). Orientation relationships between the beta bcc solid solution and C15 TiCr2 Laves phase are understood in terms of geometrical packing, and are consistent with a Laves phase growth mechanism involving twinning.
引用
收藏
页码:1472 / 1480
页数:9
相关论文
共 38 条
[1]  
Aaronson H, 1970, PHASE TRANSFORMATION
[2]  
AARONSON HI, 1960, T AM I MIN MET ENG, V218, P331
[3]   DENDRITIC GROWTH OF GERMANIUM CRYSTALS [J].
BENNETT, AI ;
LONGINI, RL .
PHYSICAL REVIEW, 1959, 116 (01) :53-61
[4]   MICROSTRUCTURAL AND CRYSTALLOGRAPHIC RELATIONSHIPS IN DIRECTIONALLY SOLIDIFIED NB-CR2NB AND CR-CR2NB EUTECTICS [J].
BEWLAY, BP ;
SUTLIFF, JA ;
JACKSON, MR ;
LIPSITT, HA .
ACTA METALLURGICA ET MATERIALIA, 1994, 42 (08) :2869-2878
[5]  
BLACKBURN MJ, 1967, T METALL SOC AIME, V239, P287
[6]  
Bywater K. A., 1975, Metal Science, V9, P155, DOI 10.1179/030634575790444685
[7]   THE ELASTIC STRAIN-ENERGY OF GROWTH LEDGES ON COHERENT AND PARTIALLY COHERENT PRECIPITATES [J].
CHEN, G ;
CHEN, JK ;
LEE, JK ;
REYNOLDS, WT .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1994, 25 (10) :2073-2082
[8]  
CHEN KC, 1995, MATER RES SOC SYMP P, V364, P1401, DOI 10.1557/PROC-364-1401
[9]  
CHEN KC, 1993, MAT RES S C, V288, P373
[10]  
CHEN KC, 1996, THESIS MIT