Thermal stability and moisture resistance of C/Al2O3/Al solar absorber surfaces

被引：13

作者：

Konttinen, P ^{[1
]}

Lund, PD ^{[1
]}

机构：

[1] Helsinki Univ Technol, Adv Energy Syst Lab, FIN-02150 Espoo, Finland

来源：

SOLAR ENERGY MATERIALS AND SOLAR CELLS | 2004年 / 82卷 / 03期

关键词：

C/Al2O3/Al solar absorber; mechanical manufacturing; accelerated aging tests; hydration;

D O I：

10.1016/j.solmat.2003.12.006

中图分类号：

TE [石油、天然气工业]; TK [能源与动力工程];

学科分类号：

0807 ; 0820 ;

摘要：

Mechanically manufactured C/Al2O3/Al solar absorber surfaces were exposed to thermal stability and moisture resistance tests following the IEA Solar Heating and Cooling Programme recommendations (draft ISO/DIS 12592). The main degradation mechanism is found to be hydration of aluminium oxide to pseudoboehmite and boehmite. We estimated the absorber service lifetime (with an optical performance more than 95% of its initial) based on two literature references, where time of wetness frequency distribution of a solar collector microclimate was measured. The estimated average service lifetime in normal use was 20 or 25 years, depending significantly on the time of wetness frequency distribution of the surface. (C) 2004 Elsevier B.V. All rights reserved.

引用

页码：361 / 373

页数：13

共 14 条

[1] Accelerated life testing of solar absorber coatings:: Testing procedure and results [J].

Brunold, S ;

Frei, U ;

Carlsson, B ;

Möller, K ;

Köhl, M .

SOLAR ENERGY, 2000, 68 (04) :313-323

[2] Round robin on accelerated life testing of solar absorber surface durability [J].

Brunold, S ;

Frei, U ;

Carlsson, B ;

Möller, K ;

Köhl, M .

SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2000, 61 (03) :239-253

[3] Comparison between predicted and actually observed in-service degradation of a nickel pigmented anodized aluminium absorber coating for solar DHW systems [J].

Carlsson, B ;

Möller, K ;

Frei, U ;

Brunold, S ;

Köhl, M .

SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2000, 61 (03) :223-238

[4] Qualification test procedure for solar absorber surface durability [J].

Carlsson, B ;

Möller, K ;

Köhl, M ;

Frei, U ;

Brunold, S .

SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2000, 61 (03) :255-275

[5]

CARLSSON B, 1994, IEA SHCP TASK X

[6]

HALME J, 2000, REFLECTANCE MEASUREM

[7]

HIHARA LH, 1994, INT MATER REV, V39, P245, DOI 10.1179/095066094790151026

[8]

KOHL M, 2001, RENEW ENERG, V24, P597

[9] Mechanically manufactured selective solar absorber surfaces [J].

Konttinen, P ;

Lund, PD ;

Kilpi, RJ .

SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2003, 79 (03) :273-283

[10] Microstructural analysis of selective C/Al2O3/Al solar absorber surfaces [J].

Konttinen, P ;

Kilpi, R ;

Lund, PD .

THIN SOLID FILMS, 2003, 425 (1-2) :24-30

← 1 2 →