Anharmonicity and fragility in lithium borate glasses

Since the physical properties of lithium borate glasses xLi(2)O-(1-x) B2O3 (0less than or equal toxless than or equal to0.28) vary over a wide range with the composition, this binary system is particularly suitable for studying the relationship between vibrational anharmonicity and fragility. The density, the linear expansion coefficient, the longitudinal and transverse ultrasonic velocities and their respective temperature coefficients of the velocities are measured, from which the vibrational anharmonicity in lithium borate glasses is evaluated with the help of the Gruneisen parameter at the Debye cut-off frequency and the Anderson- Gruneisen parameter: these two parameters plotted vs. composition have the same characteristics with minima at xapproximate to0.08. The fragility is evaluated from the temperature width of the glass transition; the fragility also shows a minimum at xapproximate to0.08. The presence of minima at xapproximate to0.08 is ascribable to the fact that the crosslinking density between six-membered rings in the glass reaches a maximum at this composition. We show that the anharmonic parameters strongly correlate with the fragility metrics.