High-resolution transmission electron microscopy: the ultimate nanoanalytical technique

被引:58
作者
Thomas, JM
Midgley, PA
机构
[1] Univ Cambridge, Dept Mat Sci & Met, Cambridge CB2 3QZ, England
[2] UCL Royal Inst Great Britain, Davy Faraday Res Lab, London W1S 4BS, England
关键词
D O I
10.1039/b315513g
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
To be able to determine the elemental composition and morphology of individual nanoparticles consisting of no more than a dozen or so atoms that weigh a few zeptograms (10(-21) g) is but one of the attainments of modern electron microscopy. With slightly larger specimens (embracing a few unit cells of the structure) their symmetry, crystallographic phase, unit-cell dimension, chemical composition and often the valence state (from parallel electron spectroscopic measurements) of the constituent atoms may also be determined using a scanning beam of electrons of ca. 0.5 nm diameter. Nowadays electron crystallography, which treats the digital data of electron diffraction (ED) and high-resolution transmission electron microscope (HRTEM) images of minute (ca. 10(-18) g) specimens in a quantitatively rigorous manner, solves hitherto unknown structures just as X-ray diffraction does with bulk single crystals. In addition, electron tomography (see cover photograph and its animation) enables a three-dimensional picture of the internal structure of minute objects, such as nanocatalysts in a single pore, as well as structural faults such as micro-fissures, to be constructed with a resolution of 1 nm from an angular series of two-dimensional (projected) images. Very recently (since this article was first written) a new meaning has been given to electron crystallography as a result of the spatio-temporal resolution of surface phenomena achieved on a femtosecond timescale.
引用
收藏
页码:1253 / 1267
页数:15
相关论文
共 102 条
[1]  
Agger JR, 2001, ANGEW CHEM INT EDIT, V40, P4065, DOI 10.1002/1521-3773(20011105)40:21<4065::AID-ANIE4065>3.0.CO
[2]  
2-F
[3]   DIRECT OBSERVATION OF STRUCTURE OF REAL CRYSTALS BY LATTICE IMAGING [J].
ALLPRESS, JG ;
SANDERS, JV .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1973, 6 (JUN1) :165-190
[4]  
Anderson J. S., 1972, SURFACE DEFECT PROPE, V1, P1
[5]  
Anderson J. S., 1974, SURFACE DEFECT PROPE, V3, P1
[6]   INFINITELY ADAPTIVE STRUCTURES [J].
ANDERSON, JS .
JOURNAL OF THE CHEMICAL SOCIETY-DALTON TRANSACTIONS, 1973, (10) :1107-1115
[7]   ON POSSIBLE ROLE OF DISLOCATIONS IN GENERATING ORDERED AND DISORDERED SHEAR STRUCTURES [J].
ANDERSON, JS ;
HYDE, BG .
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1967, 28 (08) :1393-&
[8]   IDENTIFICATION AND SOME PROPERTIES OF POINT DEFECTS AND NON-BASAL DISLOCATIONS IN MOLYBDENITE SURFACES [J].
BAHL, OP ;
EVANS, EL ;
THOMAS, JM .
PROCEEDINGS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL AND PHYSICAL SCIENCES, 1968, 306 (1484) :53-+
[9]  
BERNARD J, 1980, P NAPL C ZEOL, P628
[10]  
BETGHE H, 1964, DISCUSS FARADAY SOC, V38, P79