Structure property relations in BiFeO3/BaTiO3 solid solutions

BiFeO3, when forming a solid solution with BaTiO3, shows structural transformations over the entire compositional range. Above 70 mole % of BiFeO3 the structure is rhombohedral and below 4 mole %, it is tetragonal. In between the structure is cubic. The ferroelectric T-C decreases with increasing composition of BaTiO3 and a relatively small relaxation is observed. Impedance measurements showed a structural dependence and analysis of which has clearly shown that the capacitance observed is from the bulk of the sample. Relaxation time (tau) of BiFeO3 was estimated using the relaxation times of the intermediate compositions. Magnetization measurements showed field induced ferromagnetism. As the structure becomes cubic with increasing concentration of BaTiO3, paramagnetism sets in, as evidenced by the electron spin resonance spectra. (C) 2000 American Institute of Physics. [S0021-8979(00)06501-4].